Blends of biodegradable polymers polylactic acid/thermoplastic starch/polyhydroxybutyrate (PLA/TPS/PHB) were prepared using a twin-screw extruder. The TPS content was constant (50 %) and the PHB content in the blends was gradually changed from 0 mass % to 20 mass %. TPS was prepared by melting, where a mixture of native starch, water and glycerol was fed into the twin-screw extruder. Average temperature of extrusion was 180 °C and the concentration of glycerol was 40 mass %. Influence of the PHB concentration in the blend and that of the processing technology on the mechanical and rheological properties of the PLA/PHB composition containing TPS were studied. Mechanical properties were measured 24 h after the film and monofilament preparation and also after the specific storage time to study the effect of storage on the properties. The results indicate that differences in morphology strongly influence the mechanical properties of the studied materials with identical material composition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.