Measurements of the dynamic tensile strength of aluminum and magnesium have been carried out by investigations of the spall phenomena over a wide range of temperatures, shock-wave intensities, and load durations. Free-surface velocity profiles were recorded with VISAR and used to provide the spall strength measurements. The initial temperature of samples was varied from room temperature to near the melting point. The peak compressive pressure in the shock waves was varied from 5 to 50 GPa for aluminum and from 2 to 10 GPa for magnesium. The load duration was varied by more than one order of magnitude. The free-surface velocity measurements showed a precipitous drop in the spall strength of preheated samples as temperatures approached the melting point. No significant influence of the peak pressure on the spall strength was observed. The strain-rate dependencies of the spall strength could be represented as power functions with a power index of 0.060 for aluminum and 0.072 for magnesium. Unexpectedly large amplitudes for the Hugoniot elastic limit of both aluminum and magnesium were observed at temperatures approaching the melting point.
The subject of high-energy-density (HED) states in matter is of considerable importance to numerous branches of basic as well as applied physics. Intense heavy-ion beams are an excellent tool to create large samples of HED matter in the laboratory with fairly uniform physical conditions. Gesellschaft für Schwerionenforschung, Darmstadt, is a unique worldwide laboratory that has a heavy-ion synchrotron, SIS18, that delivers intense beams of energetic heavy ions. Construction of a much more powerful synchrotron, SIS100, at the future international facility for antiprotons and ion research (FAIR) at Darmstadt will lead to an increase in beam intensity by 3 orders of magnitude compared to what is currently available. The purpose of this Letter is to investigate with the help of two-dimensional numerical simulations, the potential of the FAIR to carry out research in the field of HED states in matter.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.