We have investigated photoconductivity and mobility in TlBr from –30 ΩC up to +20 ΩC, where the ionic conductivity is pronounced. Mobility‐related conductivity maximum superimposed on an interband‐generation conductivity growth was observed. It could be caused by the recharge of the scattering centre at about 1.65 eV. From spectral dependencies defect‐related transitions at 0.55; 0.83, 1.1; 1.32 and 1.65 eV were identified, being dependent on sample prehistory, i.e., its excitation by light and/or voltage. The transient photocurrent kinetics has demonstrated a complex behaviour that could be explained by the combined influence of electron generation/recombination processes superimposed upon the ionic conductivity. The thermally activated ionic conductivity was still effective at –20 ΩC. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)

No abstract

No abstract

No abstract

В даній роботі проведено дослідження фотоіндукованої генерації третьої гармоніки в сполуках TlCIIIDIV2X6  Для фотоіндукуючого збудження було використано різні типи лазерів з однаковою потужністю: ГДГ Nd:YAG лазера (532 нм), фундаментальний промінь Nd:YAG лазера (1064 нм) та IЧ-мікросекундний CO2 лазер з довжиною хвилі 9400 нм. Встановлено, що для кристалів TlInGe2S6 та TlGaSn2Se6 спостерігається можливість модулювати інтенсивність сигналу ГТГ, що дозволяє розглядати ці сполуки як новий тип нелінійно-оптичних лазерних модуляторів.