No abstract

No abstract

Hydrogels, three-dimensional hydrophilic water-insoluble polymer networks having mechanical properties inherent for solids, have attracted continuous research attention over a long time period. Here, we studied the structure and properties of hydrogel based on gelatin, κ-carrageenan and CNTs using the combination of SAXS, PXRD, AFM microscopy, SEM and rheology methods. We have shown that the integration of polysaccharide and protein in the composite hydrogel leads to suppression of their individual structural features and homogenization of two macromolecular components into a single structural formation. According to obtained SAXS results, we observed the supramolecular complex, which includes both polysaccharide and protein components associated with each other. It was determined that hydrogel structure formed in the initial solution state (dispersion) retains hydrogel supramolecular structure under its cooling up to gel state. The sizes of dense cores of these polyelectrolyte complexes (PEC) slightly decrease in the gel state in comparison with PEC water dispersion. The introduction of CNTs to hydrogel does not principally change the type of supramolecular structure and common structural tendencies observed for dispersion and gel states of the system. It was shown that carbon nanotubes embedded in hydrogel act as the supplementary template for formation of the three-dimensional net, giving additional mechanical strengthening to the studied system.

No abstract

Structural aspects of polysaccharide hydrogels based on sodium alginate and divalent cations Ba2+, Ca2+, Sr2+, Cu2+, Zn2+, Ni2+ and Mn2+ was studied using data on hydrogel elemental composition and combinatorial analysis of the primary structure of alginate chains. It was shown that the elemental composition of hydrogels in the form of freezing dried microspheres gives information on the structure of junction zones in the polysaccharide hydrogel network, the degree of filling of egg-box cells by cations, the type and magnitude of the interaction of cations with alginate chains, the most preferred types of alginate egg-box cells for cation binding and the nature of alginate dimers binding in junction zones. It was ascertained that metal–alginate complexes have more complicated organization than was previously desired. It was revealed that in metal–alginate hydrogels, the number of cations of various metals per C12 block may be less than the limiting theoretical value equal to 1 for completely filled cells. In the case of alkaline earth metals and zinc, this number is equal to 0.3 for calcium, 0.6 for barium and zinc and 0.65–0.7 for strontium. We have determined that in the presence of transition metals copper, nickel and manganese, a structure similar to an egg-box is formed with completely filled cells. It was determined that in nickel–alginate and copper–alginate microspheres, the cross-linking of alginate chains and formation of ordered egg-box structures with completely filled cells are carried out by hydrated metal complexes with complicated composition. It was found that an additional characteristic of complex formation with manganese cations is the partial destruction of alginate chains. It has been established that the existence of unequal binding sites of metal ions with alginate chains can lead to the appearance of ordered secondary structures due to the physical sorption of metal ions and their compounds from the environment. It was shown that hydrogels based on calcium alginate are most promising for absorbent engineering in environmental and other modern technologies.