A series of novel poly(CLMA-co-HEA)/silica nanocomposites is synthesized from caprolactone 2-(methacryloyloxy)ethyl ester (CLMA) and 2-hydroxyethyl acrylate (HEA) as organic comonomers and the simultaneous sol-gel polymerization of tetraethyloxysilane (TEOS) as silica precursor, in different mass ratios up to a 30 wt% of silica. The nanocomposites are characterized as to their mechanical and thermal properties, water sorption, bioactivity and biocompatibility, reflecting the effect on the organic matrix provided by the silica network formation. The nanocomposites nucleate the growth of hydroxyapatite (HAp) on their surfaces when immersed in the simulated body fluid of the composition used in this work. Proliferation of the MC3T3 osteoblast-like cells on the materials was assessed with the MTS assay showing their biocompatibility. Immunocytochemistry reveals osteocalcin and type I collagen production, indicating that osteoblast differentiation was promoted by the materials, and calcium deposition was confirmed by von Kossa staining. The results indicate that these poly(CLMA-co-HEA)/silica nanocomposites could be a promising biomaterial for bone tissue engineering.

Electroconductive materials based on poly(lactic acid) (PLA) electrospinning membranes grafted with carbon nanotubes (CNTs) functionalized with the carboxylic group R–COOH have been obtained. PLA electrospun membranes were modified with sulfuric acid (H2SO4) to oxidize its surface to subsequently graft the CNTs, the treatment time and drying of the membranes before grafting with CNTs being critical, influencing the final properties of the materials. SEM images showed that CNTs presented a uniform distribution on the surface of the PLA nanofibers, while FTIR spectra of PLA-CNTs materials revealed characteristic hydroxyl groups, as evidenced by absorption peaks of CNTs. Thanks to the grafting with CNTs, the resulting PLA-CNTs membranes present an improvement of the mechanical and conductive properties when compared with PLA membranes. On the one hand, grafting with CNTs causes the nanofibers to have greater rigidity, so they are more manipulable and can more easily preserve their conformation when stress is exerted. On the other hand, grafting with CNTs allows elimination of the insulating barrier of the PLA, reducing the resistivity and providing high electrical conductivity to the PLA-CNTs membranes. The incorporation of CNTs into PLA electrospun membranes is expected to offer greater functionalities to electrospun composite nanofibers for medical and industrial applications.