The local deformation process of blanks in the form of thin discs from VT6S titanium alloy with the use of pulse heating by electric current and deformation in heated state in the electrodes of the point contact welding machine is studied. The rational values of the process parameters (pulse current, pulse duration and precipitation force) are defi ned. Analysis of the microstructure for the VT6S alloy in its original state and after deformation with heating did not reveal signifi cant increase in grain and the formation of thick alpha layer. The increasing in the plasticity of the VT6S alloy after passing of the current pulse is established. At the same time, in the structure of the deformed zone noted the presence of double.

Получены порошки и керамические композиционные материалы в системе ZrO 2-Al 2 O 3 с содержанием Al 2 O 3 10 и 20 мас. %. Исследовано влияние введения оксида железа в керамические материалы ZrO 2-Al 2 O 3 на величину линейной усадки, фазовый состав, пористость, микроструктуру и механические свойства. Показано, что введение оксида железа приводит к существенному росту линейной усадки и достижению пористости ниже 1% уже при 1450°С для обоих композиционных материалов. При этом введение добавки в малых количествах стабилизирует тетрагональную модификацию ZrO 2 , в то время как рост содержания Fe до 3 мол. % приводит к увеличению количества моноклинной модификации. Получены плотноспеченные керамические материалы при 1450°С с прочностью до 760 МПа для ZrO 2-10% Al 2 O 3 и 475 МПа для ZrO 2-20% Al 2 O 3 .

No abstract