The effect of various cooling regimes on the evolution of the crystal structure of entropy- stabilized oxides (MgNiCoCuZn)O has been studied using a high-resolution time-of-flight neutron Fourier diffractometer. It has been established that cooling in a furnace at a rate of 1, 2, and 5 K/min leads not only to the segragation of a part of copper oxide into a separate phase, but also to nanostructuring of both the main matrix and CuO. The characteristic sizes of the formed nanoparticles are determined. It is shown that the expected rhombohedral or tetragonal distortions due to the possible Jahn-Teller effect are not observed in these samples.

Эволюция структурных фаз и микроструктурного литого состояния составов Fe100-(x+y)GaxAly в диапазоне 17≤(x+y)≤39 at.% изучена в нейтронных дифракционных экспериментах, выполненных с высоким разрешением и в режиме непрерывного сканирования по температуре при нагреве до ~ 900oС и последующем охлаждении. Установлено, что структуры литых состояний тройных сплавов в изученном диапазоне содержания Ga и Al в основных чертах повторяют структуру двойных составов Fe100-xGax до x~ 30 и Fe100-yAly до y~ 50. А именно, в них наблюдаются только кубические фазы (А2, D03 и B2), а гексагональные (A3, D019) и моноклинные (типа Fe13Ga9 или α-Fe6Ga5) фазы, характерные для системы Fe-Ga, отсутствуют. Расширение диапазона образования кубических фаз, образующихся на основе ОЦК-ячейки, в тройных сплавах по сравнению с Fe100-xGax, свидетельствует о роли Al в стабилизации этих структур. Ключевые слова: сплавы Fe-Ga, Fe-Al, Fe-Ga-Al, структурные фазовые переходы, дифракция нейтронов, магнитострикция.