A {001} 100 oriented aluminum single crystal was deformed by nine cycles of accumulative roll bonding which corresponded to a total equivalent strain of ε=7.2. The formation of {4 4 11} 11 11 8 component in deformation texture was examined by using electron back-scatter diffraction method. The specimen processed by five cycles ARB (ε=4) developed four variants of {123} 634 orientation in the deformation texture. Between the five and nine cycles, the four variants of {123} 634 rotated toward {4 4 11} 11 11 8 and {112} 111 orientations. The specimen after the ninth cycle had a weak texture which was mainly composed of {4 4 11} 11 11 8 , {112} 111 and {123} 634 components. The results obtained in the present study indicate that {4 4 11} 11 11 8 and {112} 111 become the primary and secondary stable orientations in the specimens deformed by accumulative roll bonding to the extremely high strain. The occurrence of the cyclic ratcheting which was reported by Heason et al. was also investigated. The cyclic ratcheting, which causes the formation of {4 4 11} 11 11 8 in the center layer, did not have much effect on the {001} 100 oriented single crystal.

No abstract

No abstract