Combustion of Ferrosilicon–Zircon Mixtures in Nitrogen Gas: Impact of Aluminum Additives

Abstract: Products formed upon combustion of [40 FeSi + 30 FeSiN + 30 ZrSiO 4 (zircon)] + xAl (x = 1.0-10, all figures in wt %) mixtures in nitrogen gas under pressure were characterized by XRD and SEM, with special emphasis on the impact of aluminum additives. Nitrogen content of combustion products and burning velocity were measured as a function of Al content x, nitrogen pressure P and sample diameter ∅. Stable frontal combustion observed at x = 6%, P = 4 MPa, and ∅ = 35 mm was found to yield a product containing β-

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...
1

Citation Types

0
0
0
1

Year Published

2022
2022
2024
2024

Publication Types

Select...
3
1
1

Relationship

0
5

Authors

Journals

citations
Cited by 5 publications
(1 citation statement)
references
References 23 publications
0
0
0
1
Order By: Relevance
“…В работе [5] представлены результаты влияния добавок алюминия (1-10 мас.% * ) на закономерности горения и фазовый состав продуктов при азотировании смеси состава «40 % ферросилиций -30% азотированный ферросилиций -30% циркон» (базовая смесь) методом СВС. ( * -Здесь и далее указаны массовые проценты).…”
Section: Introductionunclassified
“…В работе [5] представлены результаты влияния добавок алюминия (1-10 мас.% * ) на закономерности горения и фазовый состав продуктов при азотировании смеси состава «40 % ферросилиций -30% азотированный ферросилиций -30% циркон» (базовая смесь) методом СВС. ( * -Здесь и далее указаны массовые проценты).…”
Section: Introductionunclassified