Comparison of cyclic fatigue resistance of heat-treated nickel-titanium reciprocating instruments at the intracanal temperature

Abstract

Summary Background/Aim: The aim of the present study was to compare the cyclic fatigue resistance of NiTi files running with reciprocal motion and having different characteristics (RPC Blue, WOG, EndoArt Wise Reciproc Gold, EndoArt Wise Reciproc Blue) at the intracanal temperature (35°C) by using NaOCl irrigation solution. Material and Methods: Totally 60 WaveOne GOLD (Dentsply-Sirona, Ballaigues, Switzerland), Reciproc Blue (VDW, Munich, Germany), EndoArt Wise Reciproc Gold, and EndoArt Wise Blue (Inci Dental Productions Co, Istanbul, Turkey) (n= 15) files were used. Each of the rotary files were tested at the intracanal temperature (35°C) using a dynamic model in a stainless-steel artificial canal with an inner diameter of 1.5 mm, 60° angle of curvature, and 2mm radius of curvature until fracture occurred. The device automatically stopped at the moment of fracture and the number of cycles to the fracture was calculated as per second. The lengths of fractured parts were measured using a digital microcaliper. The One-Way Analysis of Variance (ANOVA) and Tukey’s post-hoc tests were used for intergroup comparisons. Results: In 2 mm Radius of curvature, the EndoArt Wise Reciproc Blue group had a significantly higher time to fracture followed by the EndoArt Wise Reciproc Gold, Resiproc Blue, WaveOne Gold. No significant difference was found between EndoArt Wise Reciproc Gold and Resiproc Blue groups (P>0.05). Among the groups, there was no statistically significant difference in the lengths of fractured parts of the instruments (P> 0.05). Conclusions: EndoArt Wise Reciproc Blue files exhibited significantly higher cyclic fatigue resistance compared with other files tested in a 2-mm radius of curvature and a 60° angle in an artificial canal at the intracanal temperature.