Comparison of the Properties of Nickel Coatings Reinforced with Dispersion SiC Particles of Micrometric, Submicrometric and Nanometric Size Deposited on the 5xxx Series Aluminium Alloy

Abstract

In this study, Ni-SiC composite coatings were electroplated on the 5xxx series aluminium alloy substrate. The effect of the quantity (25g/l i 50g/l) and the size (3µm, 0,41µm and 50nm) of SiC particles introduced into the bath as a dispersed phase on properties of the coatings was tested. The influence of these parameters on thickness, microhardness, surface structure, abrasion resistance and corrosion resistance of nickel composite coatings was determined.Keywords: nickel coatings, Ni-SiC, composite coating W niniejszej pracy powłoki Ni-SiC, osadzano elektrolitycznie na stopie aluminium serii 5xxx. Przedstawiono wyniki badań dotyczące wpływu ilości (25g/l i 50g/l) oraz wielkości cząstek SiC (3µm, 0,41µm oraz 50nm), wprowadzanych do kąpieli niklowych jako faza zdyspergowana, na właściwości otrzymanej powłoki niklowej. Określono wpływ tych parametrów na grubość, mikrotwardość, strukturę powierzchni, odporność na ścieranie oraz odporność korozyjną otrzymanych kompozytowych powłok niklowych.