Conditions of Liquid Steel Treatment for Near Net‐Shape Casting Processes

Abstract

Slab casting for hot rolled steel and strip casting using the twin roll casting (TRC) method are compared in terms of inclusions evolution.There are differences of the processes, mainly the use of casting flux in CC of slabs, or pool shapes and sizes in terms of TRC, particularly when roll diameters vary. The inclusion evolution of alumina in a low carbon steel grade was estimated. By modelling particle growth rate, coagulation and deposition, an 'agglomeration index' was created to describe the probability of clogging in the SEN. Similarly the growth of secondary alumina precipitation during cooling of the melt in the pool by Stokes collision and turbulent collision was estimated in terms of forming large particles which are able to float-up. Influences of melt superheat or caster size were taken into account. Prozessparameter fur Stahlschmelzen beim endabmessungsnahen GieBen. Das BrammenstranggieBen fOr die Warmbancferzeugung und das BandgieBen nach dem Zweirollen-Vertahren werden in Bezug auf die Einschlussbildung verglichen. Die Prozessunterschiede liegen in der Hauptsache in der Anwendung von GieBpulver beim Brammenstrangguss und in der PoolgroBe und -form beim Zweirollen-bandgieBen, insbesondere wenn der Rollendurchmesser variiert wird. Die Entwicklung von TonerdeeinschlOssen in einem weichen Kohlenstoffstahl wurde abgeschatzt. In die Modellierung der Teilchenwachstumsrate, Koagulation und Abscheidung wurde ein .Agglomerationsindex" eingefOhrt, der zur Vorhersage des Zusetzens von Tauchrohren genutzt werden kann. In ahnlicher Weise wird das Wachstum von Sekundar-Tonerdeausscheidungen durch Stokes-Kottision und turbulente Kollision wahrend der AbkOhlung der Schmelze abgeschatzt, um die Bildung groBerer, abscheidbarer EinschlOsse zu beschreiben. EinflOsse der Schmelzenuberhitzung und der GieBanlagengroBe wurden be-rOcksichtigt.