CTOA Measurements of Welds in X100 Pipeline Steel

Abstract

A suite of tests characterizing X100 pipeline steels was initiated at the National Institute of Standards and Technology (NIST) in Boulder. Part of the test matrix included testing the toughness of the base metal, welds, and heat-affected zones (HAZ) by use of modified double cantilever beam specimens for crack tip opening angle (CTOA) testing. The thickness of the test section was either 3 mm or 8 mm. Girth welds perpendicular to the growing crack, and seam welds and their HAZ parallel with the crack, were tested with a crosshead displacement rate of 0.02 mm/s (with the exception of one girth weld specimen for each thickness, which were tested at 0.002 mm/s). Analysis of the data revealed some general differences among the weld specimens. The tests where the crack ran perpendicular to the girth weld demonstrated changes in CTOA and crack growth rate as the crack moved through the base metal, HAZ, and weld material. We observed the values for CTOA increasing and the crack propagation slowing as the crack moved through the weld and approached the fusion line.