Effect of Gelatin On The Corrosion Resistance Of Cr-ZrO₂ Coatings In 3% NaCl Solution

Abstract

In this work, Cr-ZrO2 composite coating were prepared by electrodeposition method on aluminium substrate from chromic acid based electrolytes containing gelatin. The effect of gelatin on the corrosion resistance of Cr-ZrO2 coatings were studied in 3 wt.% sodium chloride solutions. Potentiodynamic polarization studies were performed using a Versastat 3 (Princeton Applied Research) electrochemical system with a three-electrode cell. Results shows that the corrosion resistance of Cr-ZrO2 coating on Al substrate was improved by the addition of gelatin to the coating solution. The addition of gelatin shifted the potentiodynamic polarization curved in the noble direction. The corrosion potential changed positively from -778 mV to -259 mV. The corrosion rate of Cr-ZrO2 coating decreased from 4.44±0.93 mpy to 0.13±0.01 mpy with the addition of 3g/L gelatin.

Technical-economical assessment of solar PV systems on small-scale fishing vessels

“…In the use of PV in areas prone to oxidation, it is necessary to pay attention to the equipment so that it is not easily corroded due to weather. This needs to be considered so that PV can be used for a long time [29]- [33].…”