Effect of P2O5 Impurities and Fluoride Ions on The Rheological Properties of Porous Glasses and Bismuth-Containing Composites Based on Them

Abstract

The results of a study of the rheological properties (shrinkage on heating, viscosity) of porous glasses (PGs) obtained as a result of through acid leaching of two-phase sodium borosilicate glass doped with small additives of P2O5 and fluoride ions, as well as bismuth-containing PGs and quartzoid glasses based on them, depending on the temperature of the heat treatment of the PG and in comparison with the characteristics of the samples obtained from sodium borosilicate glass without additives, are presented. It is found that doping glass with the indicated impurities leads to a decrease in the thermal resistance of the obtained PGs and bismuth-containing PGs. The introduction of bismuth nitrate into PG in the case of the low-temperature treatment (at 120°C) lowers the temperature for the same viscosity values of quartzoid glasses by 15–20°C, in contrast to samples without additives, as well as from higher-temperature treatment (at 650°C) PGs with additives.