Effects of Gamma-Ray Irradiation on Hardened Cement Mortar

Abstract

The effect of gamma-ray irradiation on cement mortar properties is investigated in this study in order to understand the mechanism behind the strength and stiffness reduction, which may be significant according to the available researches. 60Co irradiation facility with the generating dose rate of 0.1–10 Gy/s and the total activity of 4.4·1015 Bq (120 kCi) was used to perform the irradiation, so that the total observed dose of the irradiated samples reached the values ranging from 12.0 to 15.0 MGy. An identical set of control samples was placed in the same laboratory conditions away from gamma radiation. The results of nanoindentation, X-ray diffraction analysis and mercury intrusion porosimetry of the irradiated and the control samples are shown and explained in detail in this study. The nanoindentation creep compliance and the nanoindentation elastic modulus of the irradiated and the control samples do not show any significant difference. The mineral composition obtained using the X-ray diffraction analysis of the irradiated and the control samples is also similar. The pore structure rearrangement and microcrack occurrence, which were evidenced by the mercury intrusion porosimetry and scanning electron microscopy, led to the porosity increase and may be attributed to the significant decrease of compressive strength.

Early Age Hardening of Concrete with Heavy Aggregate in Gamma Radiation Source – Impact on the Modulus of Elasticity and Microstructural Features

“…Preliminary tests on the use of gamma radiation during the setting and early hardening of cement mortar revealed a tendency to increase the early strength (Khmurovska et al 2020). The results indicate a local densification of cement matrix, resulting in reduced capillary porosity (Burnham et al 2016).…”