Experimental Determination of Sound Transmission Loss of Some Wood Species

Abstract

Aim of study: To determine the sound transmission losses of 16 different wood species with the different density in the range of 100-1000 Hz frequencies, and the relationship between density and transmission loss was. Material and methods: In this study sound transmission loss values of Ash (Fraxinus excelsior), Acacia (Robinia pseudoacacia L.), Beech (Betula pendula), Black pine (Pinus nigra), Black poplar (Populus nigra), Canadian poplar (Populus x euramaricana), Chestnut (Castanea sativa Mill.), Cypress (Cupressus sempervirens), Oriental beech (Fagus orientalis Lips,) Eucalyptus C. (E, camaldulensis Dehnh), Eucalyptus G. (Eucalyptus grandis), Juniper (Juniperus excelsa), Plane (Platanus orientalis L.), Scotch pine (Pinus sylvetris L), Turkish Red pine (Pinus brutia Ten) and White Oak (Quercus alba) wood specimens were determined by using the impedance tube kit. Main results: Sound transmission loss is observed in lower density wood material species with the increasing frequency. However, a clear relationship has not been established between the mean sound transmission loss and density. Highlights: It is important to determine the frequency-related acoustic performance parameters of the wood material and to its relationship with density.

The effect of artificial aging on color, glossiness, pendulum hardness and adhesion to the surface of black poplar wood treated with UV curable varnish

“…Karakavak, yüksek selüloz ve nispeten düşük lignin içeriği nedeniyle kâğıt hamuru ve kağıt üretimi için uygundur (Balatinecz vd., 2001). Karakavak (Populus nigra L.) odununda, %1'lik NaOH çözünürlüğü %15.12, alfa selüloz %41.17, holoselüloz %28.46 (Narlıoğlu, 2012), Trametes versicolor mantarına karşı ağırlık kaybı %28.59 (Hashemi vd., 2010), hava kurusu yoğunluk 396 kg/m 3 , eğilme direnci 75.10 N/mm 2 , elastikiyet modülü 5438.00 N/mm 2 , basınç direnci 42.00 N/mm 2 , şok direnci 0.438 kgm/cm 2 (Bal & Ayata, 2020), ısı iletkenlik değeri 0.109 k(W/mK) (Çavuş vd., 2019), ses iletim kaybı 24.92 dB (Çavuş & Kara, 2020)…”

Sound transmission loss of LC3-based mortars with barite and waste rubber

“…14 In literature, the sound transmission loss is defined as the ratio of the incident sound power and transmitted sound power in terms of decibel (dB). 15 As the sound wave travels, differences in the rear surface and front surface of the material damp the sound wave and thus reduce the intensity of the transmitted sound power. Hence, sound transmission loss is also closely related to the damping properties of the material.…”

UVB-313 Lambalarına Ait Yapay Yaşlandırmanın UV Sistem Vernikli Yalancı Akasya Odununda Bazı Yüzey Özellikleri Üzerine Etkileri

“…Yalancı akasya odununda hava kurusu yoğunluk 828.07 g/cm 3 , öz odununda lignin %24.56, selüloz %50.53, α-selüloz %60.53, holoselüloz %78.50, kül %0.21, diri odununda lignin %23.90, selüloz %49.31, α-selüloz %63.27, holoselüloz %80.71, kül %0.41 [23], ısı iletkenlik değeri 0.166 W/m.K [24], 100'den 1000'e Hz frekans aralığında ses iletim kaybı değeri ortalama 25.46 dB ve yoğunluğu 0.731 g/cm 3 [25], çivi tutma direnci sırasıyla radyal, teğet ve enine yüzeylerde 13.75 N/ mm 2 , 10.01 N/mm 2 ve 10.51 N/mm 2 [26], shore D sertlik değeri 79. 35, eğilme direnci 189.11 N/mm 2 , şok direnci 1.740 kgm/cm 2 , eğilmede elastikiyet modülü 14128.50 N/mm 2 , vida tutma kapasitesi teğet, radyal ve enine yüzeyler için sırası ile 53.53 N/mm 2 , 52.02 N/mm 2 ve 45.10 N/mm 2 [27] olarak elde edilmiştir.…”