Functionalized graphene/thermoplastic polyester elastomer nanocomposites by reactive extrusion‐based masterbatch: preparation and properties reinforcement

Abstract

A reactive extrusion process was developed to fabricate polymer/graphene nanocomposites with good dispersion of graphene sheets in the polymer matrix. The functionalized graphene nanosheet (f-GNS) activated by diphenylmethane diisocyanate was incorporated in thermoplastic polyester elastomer (TPEE) by reactive extrusion process to produce the TPEE/f-GNS masterbatch. And then, the TPEE/f-GNS nanocomposites in different ratios were prepared by masterbatchbased melt blending. The structure and morphology of functionalized graphene were characterized by Fourier transform infrared, X-ray photoelectron spectroscopy, X-ray diffraction and transmission electron microscopy (TEM). The incorporation of f-GNS significantly improved the mechanical, thermal and crystallization properties of TPEE. With the incorporation of only 0.1 wt% f-GNS, the tensile strength and elongation at break of nanocomposites were increased by 47.6% and 30.8%, respectively, compared with those of pristine TPEE. Moreover, the degradation temperature for 10 wt% mass loss, storage modulus at À70°C and crystallization peak temperature (T cp ) of TPEE nanocomposites were consistently improved by 17°C, 7.5% and 36°C. The remarkable reinforcements in mechanical and thermal properties were attributed to the homogeneous dispersion and strong interfacial adhesion of f-GNS in the TPEE matrix. The functionalization of graphene was beneficial to the improvement of mechanical properties because of the relatively well dispersion of graphene sheets in TPEE matrix, as suggested in the TEM images. This simple and effective approach consisting of chemical functionalization of graphene, reactive extrusion and masterbatch-based melt blending process is believed to offer possibilities for broadening the graphene applications in the field of polymer processing.

Simultaneous Reduction and Functionalization of Graphene Oxide by 4-Hydrazinobenzenesulfonic Acid for Polymer Nanocomposites

“…The epoxy based HBS-rGO composite was prepared by solution mixing method [ 33 , 34 , 35 ]. The desired amount of HBS-rGO was first dispersed in ethanol via ultrasonication for 2 h. The calculated amount of epoxy resin was dissolved in ethanol under constant stirring.…”

Property improvements of thermoplastic copolyester with a multifunctional mixture/nanofiller by reactive extrusion

“…The improvement in E ″ was about 2.3% of HC1‐C2, but only 1.7% for the HC2 nanocomposite. This occurrence can be assigned to the uniform dispersion of reactive nanofiller in the host polymer, which acts as a chemical and physical crosslink …”

Modified treatment for carbonized cellulose nanofiber application in composites

“…In addition, surface modification of CNFs is also important due to the normally poor compatibility between CNFs and the matrix. Reactive extrusion is always carried out in an extruder, which encourages the generation of new chemical bonds through a melt phase reaction [34,35]. Just as usefully, reactive extrusion is an effective method to improve the compatibility between CNF filler and the matrix [36,37].…”