Improved mechanical properties of dense β-Si3N4 ceramics fabricated by spark plasma sintering with Al2O3-YSZ additives

Abstract

In this work the influence of sintering conditions on structure and mechanical properties of Si3N4 ceramics was investigated. Nearly full dense β-Si 3 N 4 ceramics with excellent mechanical properties and interlock microstructure of elongated grains was fabricated using Al 2 O 3 and yttria-stabilized zirconia (YSZ with 3 mol% Y 2 O 3) as sintering additives by spark plasma sintering (SPS) at relatively low temperature of 1600°C for 15 min. X-ray diffraction analysis shows that the SPSed sample is pure β-Si 3 N 4 phase without any secondary crystalline phase. The elements Al, Zr, Y and O of the additive can diffuse into Si 3 N 4 lattice forming β-Si 3 N 4based solid solution. The residual additive formed an amorphous phase at the β-Si 3 N 4 grain boundaries. The β-Si 3 N 4 ceramics obtained by SPS using 6.0 wt.% Al 2 O 3 and 6.0 wt.% YSZ as additives shows interlock elongated β-Si 3 N 4 grains of 500 nm in width and 3000 nm in length, high density of 3.29 g/cm 3 , Vickers hardness of 16.15 GPa and high fracture toughness K IC of 6.75 MPa m 1/2 .