In vitro analysis of the influence of surface treatment of dental implants on primary stability

Abstract

In vitro analysis of the influence of surface treatment of dental implants on primary stability Abstract: Surface treatment interferes with the primary stability of dental implants because it promotes a chemical and micromorphological change on the surface and thus stimulates osseointegration. This study aimed to evaluate the effects of different surface treatments on primary stability by analyzing insertion torque (IT) and pullout force (PF). Eight samples of implants with different surface treatments (TS -external hexagon with acid surface treatment; and MS -external hexagon, machined surface), all 3.75 mm in diameter × 11.5 mm in length, were inserted into segments of artificial bones. The IT of each sample was measured by an electronic torquemeter, and then the pullout test was done with a universal testing machine. The results were subjected to ANOVA (p < 0.05), followed by Tukey's test (p < 0.05). The IT results showed no statistically significant difference, since the sizes of the implants used were very similar, and the bone used was not highly resistant. The PF values (N) were, respectively, TS = 403.75 ± 189.80 and MS = 276.38 ± 110.05. The implants were shown to be different in terms of the variables of maximum force (F = 4.401, p = 0.0120), elasticity in maximum flexion (F = 3.672, p = 0.024), and relative stiffness (F = 4.60, p = 0.01). In this study, external hexagonal implants with acid surface treatment showed the highest values of pullout strength and better stability, which provide greater indication for their use.

Influência da topografia de superfície nanométrica na estabilidade primária de mini-implantes dentários

“…A alteração na rugosidade dos implantes devido ao tratamento superficial possibilita maior coeficiente de atrito, contato osso/implante e torque de inserção, favorecendo a estabilidade inicial [8][9][10] .…”

The impact of the thread design compared to the impact of the surface topography on the primary stability of implants inserted into fresh pig ribs

“…According to Mazzo et al (20) acid-etched surface implants have better primary stability than the implants with machine-treated surface. Duncan et al (21) conducted an experimental study involving implants with three different surface modification.…”

Análise da superfície de implantes odontológicos submetidos a ensaio de torção.

“…A morfologia superficial dos implantes modula sua ancoragem e resposta óssea 4 , por isso, alterações, como a criação de micro rugosidades na superfície dos implantes têm sido realizadas, a fim de acelerar o processo de cicatrização do osso e aumentar a aposição óssea ao redor dos parafusos de implantes 5,6 .…”

“…A morfologia superficial dos implantes modula sua ancoragem e resposta óssea 4 , por isso, alterações, como a criação de micro rugosidades na superfície dos implantes têm sido realizadas, a fim de acelerar o processo de cicatrização do osso e aumentar a aposição óssea ao redor dos parafusos de implantes 5,6 .Para avaliar os diferentes tipos de implantes disponíveis no mercado, os ensaios mecânicos são fundamentais, pois, por meio deles, é possível analisar o desempenho do material testado, quando submetido a diferentes tensões e esforços, em diferentes tipos de substratos 7 . Esses ensaios permitem predizer a durabilidade do parafuso, quantificar o torque de inserção e o nível de adaptação prótese/ implante, através da análise da plataforma protéti-http://dx.doi.org/10.5335/rfo.v19i1.3707…”