Strain localization in microelectronic devices commonly arises from device geometry, materials, and fabrication processing. In this study, we controllably relieve the local strain field of AlGaN/GaN HEMTs by milling micro-trenches underneath the channel and compare the device performance as a function of the relieved strain as well as radiation dosage. Micro-Raman results suggest that the trenches locally relax the strain in device layers, decreasing the 2DEG density and mobility. Intriguingly, such strain relaxation is shown to minimize the radiation damage, measured after 10 Mrads of 60Co-gamma exposure. For example, a 6-trench device showed only ∼8% and ∼6% decrease in saturation drain current and maximum transconductance, respectively, compared to corresponding values of ∼15% and ∼30% in a no-trench device. Negative and positive threshold voltage shifts are observed in 6-trench and no-trench devices, respectively, after gamma radiation. We hypothesize that the extent of gamma radiation damage depends on the strain level in the devices. Thus, even though milling a trench decreases 2DEG mobility, such decrease under gamma radiation is far less in a 6-trench device (∼1.5%) compared to a no-trench device (∼20%) with higher built-in strain.
Strain localization in microelectronic devices commonly arises from device geometry, materials, and fabrication processing. In this study, we controllably relieve the local strain field of AlGaN/GaN HEMTs by milling micro-trenches underneath the channel and compare the device performance as a function of the relieved strain as well as radiation dosage. Micro-Raman results suggest that the trenches locally relax the strain in device layers, decreasing the 2DEG density and mobility. Intriguingly, such strain relaxation is shown to minimize the radiation damage, measured after 10 Mrads of 60Co-gamma exposure. For example, a 6-trench device showed only ∼8% and ∼6% decrease in saturation drain current and maximum transconductance, respectively, compared to corresponding values of ∼15% and ∼30% in a no-trench device. Negative and positive threshold voltage shifts are observed in 6-trench and no-trench devices, respectively, after gamma radiation. We hypothesize that the extent of gamma radiation damage depends on the strain level in the devices. Thus, even though milling a trench decreases 2DEG mobility, such decrease under gamma radiation is far less in a 6-trench device (∼1.5%) compared to a no-trench device (∼20%) with higher built-in strain.
Strain plays an important role in the performance and reliability of AlGaN/GaN high electron mobility transistors (HEMTs). However, the impact of strain on the performance of proton irradiated GaN HEMTs is yet unknown. In this study, we investigated the effects of strain relaxation on the properties of proton irradiated AlGaN/GaN HEMTs. Controlled strain relief is achieved locally using the substrate micro-trench technique. The strain relieved devices experienced a relatively smaller increase of strain after 5 MeV proton irradiation at a fluence of 5 × 1014 cm−2 compared to the non-strain relieved devices, i.e., the pristine devices. After proton irradiation, both pristine and strain relieved devices demonstrate a reduction of drain saturation current (Ids,sat), maximum transconductance (Gm), carrier density (ns), and mobility (μn). Depending on the bias conditions the pristine devices exhibit up to 32% reduction of Ids,sat, 38% reduction of Gm, 15% reduction of ns, and 48% reduction of μn values. In contrast, the strain relieved devices show only up to 13% reduction of Ids,sat, 11% reduction of Gm, 9% reduction of ns, and 30% reduction of μn values. In addition, the locally strain relieved devices show smaller positive shift of threshold voltage compared to the pristine devices after proton irradiation. The less detrimental impact of proton irradiation on the transport properties of strain relieved devices could be attributed to reduced point defect density producing lower trap center densities, and evolution of lower operation related stresses due to lower initial residual strain.
Thermal annealing is a widely used strategy to enhance semiconductor device performance. However, the process is complex for multi-material multi-layered semiconductor devices, where thermoelastic stresses from lattice constant and thermal expansion coefficient mismatch may create more defects than those annealed. We propose an alternate low temperature annealing technique, which utilizes the electron wind force (EWF) induced by small duty cycle high density pulsed current. To demonstrate its effectiveness, we intentionally degrade AlGaN/GaN high electron mobility transistors (HEMTs) with accelerated OFF-state stressing to increase ON-resistance ∼182.08% and reduce drain saturation current ∼85.82% of pristine condition at a gate voltage of 0 V. We then performed the EWF annealing to recover the corresponding values back to ∼122.21% and ∼93.10%, respectively. The peak transconductance, degraded to ∼76.58% of pristine at the drain voltage of 3 V, was also recovered back to ∼92.38%. This recovery of previously degraded transport properties is attributed to approximately 80% recovery of carrier mobility, which occurs during EWF annealing. We performed synchrotron differential aperture x-ray microscopy measurements to correlate these annealing effects with the lattice structural changes. We found a reduction of lattice plane spacing of (001) planes and stress within the GaN layer under the gate region after EWF annealing, suggesting a corresponding decrease in defect density. Application of this low-temperature annealing technique for in-operando recovery of degraded electronic devices is discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2025 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.