Pembuatan Roda Gigi Dari Bahan Serbuk Logam Tembaga Dan Alumunium Dengan Proses Kompaksi

Alfauzi, Abdul Syukur; Purnomo, Adhy; Tjahjono, Bambang; Hariyanto, Hariyanto; Sa’adah, Nur

doi:10.32497/jrm.v14i3.1641

Cited by 3 publications

(2 citation statements)

References 1 publication

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Penelitian diawalai dengan pengamatan dilapangan dimana berupaya untuk mendapatkan metode farbikasi yang lebih efekti. Dari studi literatur dinyatakan bahwa metode metalurgi serbuk secara umum lebih efisien dibanding dengan metode lain karena metode ini tidak menghasilkan limbah [6][7]. Metode ini dengan cara mencetak komponen sesuai dengan bentuk dan ukuran yang desain yang dibutuhkan.…”

Section: Metodeunclassified

SIFAT MEKANIK DAN STRUKTUR MIKRO KOMPOSIT ALUMUNIUM TEMBAGA (Al-Cu) DENGAN VARIASI KOMPOSISI

Susila

Supriyanto²,

Hermawan

2022

JTe

View full text Add to dashboard Cite

Pengembangan manufaktur senantiasa dilakukan hingga saat ini. Hal ini sebagai upaya untuk mendapatkan metode fabrikasi yang optimal. Pada penelitian ini dikembangkan pembuatan material komposit dengan menggunakan metode metalurgi serbuk. Tujuan dari pekerjaan ini adalah untuk mengetahui sifat mekanik paduan tembaga-aluminium yang dibentuk oleh metalurgi serbuk. Bahan yang digunakan dalam penelitian ini adalah serbuk aluminium murni dan serbuk tembaga. Serbuk aluminium 300 mesh sebagai matrik dan serbuk tembaga 150 mesh sebagai penguat. Serbuk aluminium dan tembaga dicampur dan diaduk selama 2 menit dengan kecepatan 95 rpm, kemudian dimasukkan ke dalam cetakan yang kemudian dipress dengan alat press hidrolik yang dilengkapi dengan manometer dengan tekanan 300 psi, 3250 psi dan 3500 psi. Sampel hasil cetakan kemudian dipanaskan (sintering) dengan variasi suhu 400oC, 500 oC, dan 600 oC. Sedangkan waktu penahanan 45 menit, 60 menit dan 75 menit. Sampel tersebut diuji kekerasan dan struktur mikro. Hasil pengujian kekerasan pada sampel 1 diperoleh nilai kekerasan rata-rata sebesar 22,32 kg/mm2. Sampel 2 diperoleh nilai kekerasan rata-rata 23,62 kg/mm2. Sampel 3 diperoleh nilai kekerasan 24,95 kg/mm2. Dari ketiga sampel tersebut, menunjukkan bahwa semakin tinggi tekanan kompaksi serta semakin tinggi suhu sintering maka semakin tinggi pula nilai kekerasan material. Selanjutnya sampel benda jadi dilakukan uji foto mirographi untuk mengetahui porositasnya. Dari hasil fotographi diperoleh sampel 1,2 dan 3 terdapat porositas yang ditandai dengan gambar berwarna kelabu. Dari gambar diketahui bahwa jumlah porositas menunjukkan variasi dari ketiga sampel. Hal ini diungkinkan karena pengaruh pengadukan (mixing) yang kurang merata (homogen).

show abstract

Section: Metodeunclassified

SIFAT MEKANIK DAN STRUKTUR MIKRO KOMPOSIT ALUMUNIUM TEMBAGA (Al-Cu) DENGAN VARIASI KOMPOSISI

Susila

Supriyanto²,

Hermawan

2022

JTe

View full text Add to dashboard Cite

show abstract

“…Alauzi dkk [4] didalam penelitiannya telah membuat roda gigi dari bahan serbuk logam tembaga dan alumunium. Dengan menggunakan proses kompaksi, green compact (GC) di tekan dengan kekuatan 6 ton kemudian disinter pada suhu 868 o C. Hasil terbaik diperoleh dengan komposisi tembaga 75% dan alumunium sebanyak 25%.…”

Section: Pendahuluanunclassified

Effect of Chromium Doping to Hardness Properties in the Manufacture of Spur Gears Made from Ferrous Powder

Saragih

Sutjipto

2020

JTM

View full text Add to dashboard Cite

A gear is a part of a machine that has a very complex shape so that it requires special care and expertise in the manufacturing process. Powder metallurgy offers an efficient manufacturing process for the production of these complex machining parts. In this study, Cr metal powder was selected to increase the hardness properties of spur gears made from iron (Fe) powder. Doping Cr by 0%; 0.5%; 10%, 1.5% and 2.0% will be added in gear manufacturing. Water is used as a binder with a ratio of 1:15 which is then packed by 15,000 kg or 15 tons then heated or sintered at a temperature of 1200 oC for 1 hour. The shrinkage ratio of the sample to the sintering treatment averaged 4.6%. 0.2 kg of load applied to the Vickers hardness test. Vickers hardness values obtained were 60, 77, 90, 184 and 211 respectively for the Cr doping of 0%; 0.5%; 10%, 1.5% and 2.0%. From these data it is found that the addition of the element Cr increases the hardness properties of iron gears. The hardness value shown is still too small, this is because there is still a lot of porosity generated in the sintering process because it is not in a vacuum condition.

show abstract

Pengaruh Doping Kromium (Cr) Terhadap Sifat Kekerasan Pada Pembuatan Roda Gigi Lurus Berbahan Serbuk Besi (Fe)

Saragih

Sutjipto

2020

Prosid Sem Nas Teknoka

View full text Add to dashboard Cite

Roda gigi adalah bagian dari mesin yang memiliki bentuk sangat kompleks sehingga diperlukan ketelitian dan keahlian khusus didalam proses pembuatannya. Metalurgi serbuk menawarkan suatu proses pembuatan yang efisien guna menghasilkan bagian-bagian permesinan yang kompleks tersebut. Pada penelitian ini dipilih serbuk logam Cr untuk meningkatkan sifat kekerasan dari roda gigi lurus berbahan dasar serbuk besi (Fe). Doping Cr sebesar 0%; 0,5%; 10%, 1,5% dan 2,0% akan ditambahakan pada pembuatan roda gigi. Air digunakan sebagai pengikat dengan ratio 1:15 yang selanjutnya dikompaksi sebesar 15,000 kg atau 15 ton diteruskan dengan dipanaskan atau sintering pada suhu 1200 oC selama 1 jam. Ratio penyusutan sampel terhadap perlakuan sintering rata-rata 4.6%. Sebesar 0.2 kg beban yang terapkan pada pengujian kekerasan Vickers. Nilai kekerasan Vickers diperoleh sebesar 60, 77, 90, 184 dan 211 masing-masing untuk doping Cr sebesar 0%; 0,5%; 10%, 1,5% dan 2,0%. Dari data tersebut didapat bahwa penambahan unsur Cr meingkatkan sifat kekerasan pada roda gigi besi. Nilai kekerasan yang ditunjukkan masih terlalu kecil hal ini disebabkan oleh masih banyak porositas yang ditimbulkan pada proses sintering karena tidak dalam kondisi vakum.

show abstract

Pembuatan Roda Gigi Dari Bahan Serbuk Logam Tembaga Dan Alumunium Dengan Proses Kompaksi

Cited by 3 publications

References 1 publication

SIFAT MEKANIK DAN STRUKTUR MIKRO KOMPOSIT ALUMUNIUM TEMBAGA (Al-Cu) DENGAN VARIASI KOMPOSISI

SIFAT MEKANIK DAN STRUKTUR MIKRO KOMPOSIT ALUMUNIUM TEMBAGA (Al-Cu) DENGAN VARIASI KOMPOSISI

Effect of Chromium Doping to Hardness Properties in the Manufacture of Spur Gears Made from Ferrous Powder

Pengaruh Doping Kromium (Cr) Terhadap Sifat Kekerasan Pada Pembuatan Roda Gigi Lurus Berbahan Serbuk Besi (Fe)