Pengaruh Lama Aktivasi Terhadap Struktur Kimia Dan Mutu Arang Aktif Serbuk Gergaji Sengon

Pari, Gustan; Sofyan, Kurnia; Syafii, Wasrin; Buchari, Buchari

doi:10.20886/jphh.2005.23.3.207-218

Cited by 8 publications

(6 citation statements)

References 0 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Di Indonesia, produksi arang secara umum memiliki keunggulan diantaranya bahan baku tersedia dalam jumlah yang cukup banyak dan dapat diambil dari berbagai dimensi dan jenis kayu seperti dari limbah industri, potongan kayu berdiameter kecil dan dari jenis kayu tidak komersial. 2 Bahan-bahan ini dapat diolah lebih lanjut menjadi hasil samping yang berguna yaitu menjadi produk arang ataupun briket arang melalui pendekatan teknologi limbah. Energi dari suatu benda adalah ukuran dari kesanggupan benda tersebut untuk melakukan suatu.…”

Section: Pendahuluanunclassified

Making Charcoal Water Electrodes

Rashidah

Tanjung

Sembiring

2021

IJCST

View full text Add to dashboard Cite

Charcoal is the residual waste from the heat decomposition process of carbon-containing materials, most of whose components are carbon. This study aims to determine the frequency of charcoal water as an electrolyte solution to produce an alternative energy source that is environmentally friendly. The method used in the experiment is to find the type of water with the addition of zinc and copper and to measure the sample voltage of charcoal water to determine the optimum mass and optimum interaction time. The variation in the volume of water with 50 ml and 100 ml of charcoal water was produced, with the addition of zinc and copper in the size of 1x5 cm, 2x5 cm, 3x5 cm which resulted in fluctuations in each data. For example, the difference in voltage value in the type of water used is tap water, 100 ml well water with the addition of zinc and copper measuring 2x5 cm. Tap water, namely with an electric voltage of 0.65 V, 0.70 V, 0.60 V, 0.60 V, 0.75 V and well water with an electric voltage of 0.60 V, 0.55 V, 0.55 V, 0.55 V, 0.55 V. Less than the maximum frequency produced with two glasses that are not made into a series or parallel circuit.

show abstract

Section: Pendahuluanunclassified

Making Charcoal Water Electrodes

Rashidah

Tanjung

Sembiring

2021

IJCST

View full text Add to dashboard Cite

show abstract

“…Namun, dari hasil penelitian yang diperoleh semakin lama waktu aktivasi karbon aktif, kadar abu yang dihasilkan semakin meningkat. Hal ini diperkuat oleh (Pari et al, 2004) menunjukkan pemakaian bahan kimia sebagai bahan pengaktif seringkali mengakibatkan pengotoran pada karbon aktif yang dihasilkan. Umumnya aktivator meninggalkan sisa-sisa yang tidak diinginkan, misalnya oksida yang tidak larut dalam air pada waktu pencucian.…”

Section: Analisa Kadar Abuunclassified

Pembuatan Karbon Aktif dari Limbah Plastik PET (Polyethylene terephthalate) Menggunakan Aktivator KOH

Oko

Mustafa

Kurniawan

et al. 2021

METANA

View full text Add to dashboard Cite

Pengunaan plastik setiap hari mengakibatkan terjadinya penumpukan sampah plastik yang dapat mencemari lingkungan dan menjadi salah satu masalah serius yang harus ditangani karena plastik tidak dapat terdegradasi. Plastik merupakan senyawa yang unsur penyusun utamanya adalah karbon dan hidrogen. Sehingga limbah plastik berpotensi sebagai pembuatan karbon aktif dan akan membuat limbah plastik menjadi lebih bermanfaat. Penelitian ini bertujuan untuk mengetahui pengaruh konsentrasi aktivator dan waktu aktivasi terhadap proses aktivasi fisika kimia sehingga menghasilkan produk karbon aktif yang sesuai dengan SNI 06-3730-1995. Plastik PET terlebih dahulu dikarbonasi pada temperatur 480oC selama 2 jam menggunakan furnace hingga membentuk arang. Lalu, direndam dalam aseton selama 24 jam. Setelah itu disaring dan dikeringkan menggunakan oven pada temperatur 110oC selama 3 jam dan dilanjutkan dengan proses aktivasi fisika pada temperatur 750oC selama 2 jam. Karbon yang telah teraktivasi fisika selanjutnya diaktivasi secara kimia dengan menggunakan KOH konsentrasi 1 M, 2 M, 3 M, dan 4M dengan variasi waktu 2 jam dan 4 jam. Diperoleh hasil terbaik yaitu pada karbon aktif dengan konsentrasi KOH 4 M dan waktu aktivasi 2 jam dengan nilai daya serap iod sebesar 980,17 mg/g, kadar abu 0,28%, kadar air 7,55%, dan kadar volatile matter 3,47%. Karbon aktif yang diperoleh telah memenuhi SNI 06-3730-1995.The use of plastic every day results in the accumulation of plastic waste that can pollute the environment and was a serious problem that must be addressed because plastic cannot be degraded. Plastic was a compound whose main constituent elements were carbon and hydrogen. So that plastic waste has the potential to produce activated carbon and will make plastic waste more useful. This study aims to determine the effect of activator concentration and activation time on the physical-chemical activation process so as to produce activated carbon products in accordance with SNI 06-3730-1995. PET plastik was first carbonated at a temperature of 480oC for 2 hours using a furnace to form charcoal. Then, soaked in acetone for 24 hours. After that it was filtered and dried using an oven at a temperature of 110oC for 3 hours and continued with the physical activation process at a temperature of 750oC for 2 hours. The physically activated carbon was then chemically activated using KOH concentrations of 1 M, 2 M, 3 M, and 4 M with time variations of 2 hours and 4 hours. The best results were obtained on activated carbon with a concentration of KOH 4 M and an activation time of 2 hours with an iodine absorption value of 980.17 mg/g, 0.28% ash content, 7.55% water content, and volatile matter levels 3,47%. Activated carbon obtained has complied with SNI 06-3730-1995.

show abstract

“…Masalah yang sering muncul dari produksi karbon aktif adalah sifat dan mutu yang cukup rendah dan penggunaanya masih sedikit, terutama karbon aktif yang berasal dari serbuk gergaji kayu (Pari, 2011). Jumlah limbah serbuk kayu gergaji yang ada di Indonesia sebesar 0,78 juta m 3 /tahun (Mutiara dkk, 2016).…”

Section: Pendahuluanunclassified

Pengaruh Jenis Aktivator Dan Ukuran Karbon Aktif Terhadap Pembuatan Adsorbent Dari Serbik Gergaji Kayu Sengon (Paraserianthes Falcataria)

Erawati

Fernando

2018

JIP UNTIRTA

View full text Add to dashboard Cite

AbstrakPenelitian ini bertujuan untuk mengetahui pengaruh jenis aktivator dan ukuran partikel terhadap karakteristik karbon aktif dari serbuk gergaji kayu sengon (Paraserianthes falcataria). Karakteristik karbon aktif perlu dilakukan pengujian untuk mengetahui kualitas adsroben, pengujian tersebut meliputi uji kadar air, kadar abu, daya serap terhadap iodin, dan BET (Braunanear, Emmelt, dan Teller). Serbuk kayu sengon yang telah dihaluskan kemudian diayak mengunakan variasi -20,+40, -40,+60, -60,+80, -80,+100 mesh. Proses karbonisasi dilakukan pada suhu 500°C selama 30 menit. Pembuatan karbon aktif diaktivasi menggunakan aktivator H3PO4, NaOH, dan NaCl dengan konsentrasi masing-masing 0,1 M dalam 100 mL. Proses aktivasi dilakukan perendaman selama 24 jam, menyaring, dan residunya dibilas dengan aquadest hingga pH netral kemudian dioven pada suhu 150°C selama 3 jam. Hasil Karbon aktif dilakukan uji kualitas sesuai dengan SNI 06-3730-1995. Hasil penelitian dalam pembuatan karbon aktif dari serbuk kayu sengon menunjukkan H3PO4 merupakan aktivator terbaik pada ukuran partikel -80,+100 mesh, menghasilkan kadar air, kadar abu, dan daya serap iodin berturut-turut sebesar 3,69%, 2,89%, dan 710,64 mg/g. Uji BET dilakukan pada ukuran partikel -60,+80 mesh sebesar 0,534 m 2 /gram. AbstractThis study aims to determine the effect of activator types and particle sizes on the characteristics of activated carbon from sengon wood sawdust (Paraserianthes falcataria). The characteristics of activated carbon need to be tested to determine the quality of adsorbent, the test includes testing of water content, ash content, the absorption capacity of iodine, and BET (Braunanear, Emmelt, and Teller). Sengon wood powder which has been mashed then sifted using variations of -20, + 40, -40, + 60, -60, + 80, -80, + 100 mesh. temperature of 500°C for 30 minutes. The activated carbon is activated using activators of H3PO4, NaOH, and NaCl with a concentration of 0.1 M in 100 ml, respectively. The activation process was soaked for 24 hours, filtered and the residue rinsed with distilled water until the pH was neutral, then oven at 150°C for 3 hours. Active carbon results are tested for quality in accordance with SNI 06-3730-1995. The results of the research in the manufacture of activated carbon from sengon wood powder showed that H3PO4 was the best activator in particle size of -80,+100 mesh, resulting in moisture content, ash content, and iodine absorption of 3.69%, 2.89%, 710.64 mg/g respectively, and . The BET test is carried out at a particle size of -60,+80 mesh of 0.534 m 2 / gram.

show abstract

Pengaruh Lama Aktivasi Terhadap Struktur Kimia Dan Mutu Arang Aktif Serbuk Gergaji Sengon

Cited by 8 publications

References 0 publications

Making Charcoal Water Electrodes

Making Charcoal Water Electrodes

Pembuatan Karbon Aktif dari Limbah Plastik PET (Polyethylene terephthalate) Menggunakan Aktivator KOH

Pengaruh Jenis Aktivator Dan Ukuran Karbon Aktif Terhadap Pembuatan Adsorbent Dari Serbik Gergaji Kayu Sengon (Paraserianthes Falcataria)