Preparation, Characterization and Osteogenic Potential of an Injectable Photo-Curable Hyaluronic Acid Hydrogel Scaffold Loaded With Bioactive Nano-Hydroxyapatite.

Abstract

Introduction: In-situ photo-cured hydrogels for bone regeneration offer an advantage compared to solid scaffolds or membranes is that it can be used by minimally invasive techniques and can fill irregularly shaped defects easily. Objective: was to prepare an injectable photo-curable hyaluronic acid hydrogel scaffold loaded with bioactive nano-hydroxyapatite using riboflavin as a natural source photoinitiator for bone regeneration and to investigate the effect of addition of nano-hydroxyapatite on the physiochemical and mechanical properties of the prepared hydrogel. Also, the osteogenic potential of the prepared hydrogels was assessed in a rabbit model. Materials and methods: Two groups were prepared, (Group I) photo-cured hyaluronic acid as a control group and (Group II) photo-cured hyaluronic acid/nano-hydroxyapatite. Laboratory Alexandria Dental Journal Volume XX. Issue X ii characterization tests: FTIR, XRD, SEM, mechanical, swelling and degradation rate tests were performed. Cell viability % using the MTT assay was used to assess the biocompatibility. In vivo bioactivity was assessed in a rabbit model and histomorphometric analysis was done. Results: Statistical analysis of results revealed that the addition of nano-hydroxyapatite increased significantly the mechanical properties of the hydrogels. SEM images demonstrated that the addition of nano-hydroxyapatite caused the formation of interconnected pores. MTT assay showed that hydrogel extract didn't affect cell viability after 48h. Histomorphometric analysis results revealed that the photo-cured (GMA-HA/HAP) hydrogel increased the osteogenic potential by one and a half folds compared to the control group and this proved its bioactivity. Conclusion: Results suggest that the prepared photo-cured hyaluronic hydrogel is a promising biomaterial to deliver bioactive nano-hydroxyapatite and has an osteogenic potential.

Histomorphometric evaluation of 3D printed graphene oxide-enriched poly(ε-caprolactone) scaffolds for bone regeneration

“…The resulted formazan crystals were then solubilized in isopropanol and the solution concentration was determined by spectrophotometry at 550 nm. The relative cell viability (%) compared to control wells was calculated using the following equation, where (A) is the absorbance and the control were wells containing cells without the scaffolds [ 17 , 20 ]: Cell viability % = (A) test/(A) control × 100 …”