Single-Crystalline, Stoichiometric Bi2Te3 Nanowires for Transport in the Basal Plane

Dielectrophoretic investigation of Bi2Te3nanowires—a microfabricated thermoelectric characterization platform for measuring the thermoelectric and structural properties of single nanowires

“…After NW assembly and EBID processes, the TNCP was introduced into a Zeiss 912 Ω TEM operated at 120 kV, and equipped with a LaB 6 gun, an Omega energy filter, and an energy-dispersive x-ray (EDX) detector. Crystallinity and grain orientation were analyzed by electron diffraction for which a selected area electron diffraction (SAED) aperture was used, selecting regions for diffraction with a diameter of 750 nm [30,31]. The size of the crystallites was (b) By heating H 1 , the temperature increase per heater power ΔT/P H1 as function of the chamber temperature T c in N 2 atmosphere is achieved.…”

“…determined by bright-and dark-field images of NWs in twobeam diffraction conditions [31]. Images and diffraction patterns were acquired with inserted energy slit aperture with 10 eV in width for enhancing contrast by filtering out inelastically scattered electrons.…”

“…Hence, the NW allows transport along the basal plane. Electron diffraction patterns (figure 11(d)) and dark-field images (figure 11(c)) under twobeam diffraction contrast conditions were acquired at various positions of the NW [31]. The NW was found to be single crystalline over its entire length of 6.5 μm in-between the Si cantilevers, no grain boundaries were detected.…”

“…The Bi 2 Te 3 NWs are synthesized by electrodeposition into porous anodic alumina membranes. The process is described elsewhere in detail [30,31].…”

FORMATION OF NANOPOROUS Al2O3 FILMS

“…Це зумовлено можливістю використання плівок анодного оксиду алюмінію в якості шаблонів або вихідних матеріалів при виготовленні різних наноструктур, таких як нанодроти, нанотрубоки та нанопористі плівки. Ці нанооб'єкти були використані в різних перспективних застосуваннях [2], таких як середовища для магнітного запису інформації [3], термоелектричні матеріали [4], оптичні матеріали [5], датчики [6,7,8,9], для зберігання енергії [10], фотокаталіз [11], фотоелектричні пристрої [12] і біоматеріали [13]. На даний час були отримані плівки ПАОА з діаметром пор в діапазоні від 4 до 250 нм, густиною вище, ніж 10 15 пор/м 2 , а товщина плівки варіюється від 0,1 до 300 мкм.…”