Strain controlled medium cycle fatigue of a notched Pb-Sn-Cd lead alloy

Abstract

During the extrusion process of subsea power cable sheathing layer it is possible that metallic and/or non-metallic debris present in the processing environment enter the metal lattice originating discontinuities that might have a detrimental effect on the fatigue life and the overall integrity of the sheathing. In order to understand the influence of these production defects on the reliability of installed power-lines, a series of specimens directly retrieved from the extruded sheathing were fatigue tested at different strain rates and range both in presence and absence of a non-passing through notch simulating the geometrical discontinuity induced by a particle. In order to collect the necessary information for the understanding of the failure mechanism, Digital Image Correlation and Scanning Electron Microscopy were used to understand the influence of the testing condition on the material resistance and failure mode.

Fracture Surface Behavior of 34CrNiMo6 High-Strength Steel Bars with Blind Holes under Bending-Torsion Fatigue

“…Efficient design and safe service operation of mechanical components subjected to cyclic loading is a constant goal of modern industry. Therefore, engineering materials with different geometries and shapes are increasingly studied under complex fatigue conditions and synergistic effects [ 1 , 2 , 3 , 4 ]. Viespoli et al [ 4 ] studied the failure mechanisms of severe geometric discontinuities in terms of creep and fatigue interaction.…”

“…Therefore, engineering materials with different geometries and shapes are increasingly studied under complex fatigue conditions and synergistic effects [ 1 , 2 , 3 , 4 ]. Viespoli et al [ 4 ] studied the failure mechanisms of severe geometric discontinuities in terms of creep and fatigue interaction. They showed that the plastic behavior of the cable resulted in a minimal notch sensitivity for cracks starting from different positions associated with lower geometrical stress concentration factors.…”