Structural and Ferroelectric Properties of Large c/a Phase Bismuth Ferrite Thin Films Prepared by Ion Beam Sputtering

Abstract

BiFeO 3 (BFO) thin films have been deposited on SrRuO 3 /SrTiO 3 (001) substrate by using ion beam sputtering process. At low oxygen partial pressure of 11 m Pa, rhombohedral and large c/a mixed phase thin film have been obtained in spite of rhombohedral BFO single phase formation at high oxygen partial pressure of 73 mPa. From wide area 2 -mappings, diffraction peaks from large c/a phase BFO thin film were obtained with the same extinction rule as those of rhombohedral BFO. Reciprocal space mappings around BFO (003) and BFO (103) spots indicate that lattice parameters of large c/a phase BFO were a = 0.381 nm and c = 0.461 nm (c/a =1.22), respectively. Moreover ferroelectric domain switching could be observed in both of rhombohedral BFO and mixed phase BFO thin films.