Synthesis and Evaluation of Eco-Friendly, Ambient-Cured, Geopolymer-Based Bricks Using Industrial By-Products

Abstract

Geopolymer-based sustainable red mud bricks (SRMBs) were cast using industrial by-products under ambient curing. The ingredients used were red mud, fly ash, ground granulated blast furnace slag and alccofine, along with quarry dust and alkali activators as binders. This paper briefly presents the characterization, strength and durability studies conducted on SRMBs. The optimization techniques were used to fix the right mix proportions. The optimized mix proportion was identified as R45F40G10A05: 45% red mud, 40% fly ash, 10% ground granulated blast furnace slag and 5% alccofine. The compressive, flexural and split tensile strength of the ambient-cured specimens after 28 days were observed as 35.38 MPa, 6.4 MPa and 1.67 MPa, respectively. The results were analysed and validated by the finite element method using Analysis of Systems (ANSYS) software. The percentage of water absorption in the SRMBs was less than 6%, and it was an entirely efflorescence-free product with a pleasing appearance and colour. Fifty percent of the targeted compressive strength was acquired after three days of ambient curing. SRMBs are a green product casted by encapsulating industrial by-products into a functional building element. Thus, SRMBs are a suitable and alternative product to conventional clay burnt bricks.

Experimental and Statistical Study of Flexural Strength in Ternary Blended High-Performance Concrete using Alcofine

“…The specific percentage of Alccofine (20%) chosen for the study may not be optimal for all conditions. Different percentages may yield different results, and the chosen proportion might not represent the best balance between performance and cost [22]. The study may not account for real-world conditions, such as construction practices, variations in field applications, and external factors that could impact the concrete's performance in actual structures.…”

Concrete for Living Walls: Current Status and a New Design Recommendation

“…Structural HPC is critical for optimizing cost, installation efficiency, and weight. The price of commercially available ultra-high-performance (UHPC) concrete mixes may range between 1500-2500 EUR/m 3 [21], mostly due to expensive steel fibres, the large amount of high-grade micro-fillers, and the use of fine quartz sand [22]. In this respect, the use of more economical HPC mixes composed of natural sand, non-pure filler materials and synthetic fibres may be economically feasible;…”

Eco-Friendly Sustainable Concrete and Mortar Using Coal Dust Waste

“…Materials 2023, 16, 6604 2 of 23 Coal dust can be classified as an inert mineral additive that does not fully react with the binder component in the concrete mixture. The main purpose of using additives of this type in concrete technology is the additional compaction of cement composites achieved by reducing porosity [11,12].…”

“…It was established that metakaolin in SCC at a rational quantity also has a positive effect on the strength, water absorption and porosity. The use of metakaolin as a partial replacement for cement in concrete technology was also studied in detail in [16][17][18][19]. It is noted that the use of this additive in rational quantities makes it possible to improve the strength characteristics and durability of composites and reduce their porosity and water absorption.…”