Synthesis of Bi2S3/BiVO4 Heterojunction with a One-Step Hydrothermal Method Based on pH Control and the Evaluation of Visible-Light Photocatalytic Performance

Abstract

The band gaps of bismuth vanadate (BiVO4) and bismuth sulfide (Bi2S3) are about 2.40 eV and 1.30 eV, respectively. Although both BiVO4 and Bi2S3 are capable of strong visible light absorption, electron–hole recombination occurs easily. To solve this problem, we designed a one-step hydrothermal method for synthesizing a Bismuth sulfide (Bi2S3)/Bismuth vanadate (BiVO4) heterojunction using polyvinylpyrrolidone K-30 (PVP) as a structure-directing agent, and 2-Amino-3-mercaptopropanoic acid (l-cysteine) as a sulfur source. The pH of the reaction solution was regulated to yield different products: when the pH was 7.5, only monoclinic BiVO4 was produced (sample 7.5); when the pH was 8.0 or 8.5, both Bi2S3 and BiVO4 were produced (samples 8.0 and 8.5); and when the pH was 9.0, only Bi2S3 was produced (sample 9.0). In sample 8.0, Bi2S3 and BiVO4 were closely integrated with each other, with Bi2S3 particles formed on the surface of concentric BiVO4 layers, but the two compounds grew separately in a pH solution of 8.5. Visible-light photocatalytic degradation experiments demonstrated that the degradation efficiency of the Bi2S3/BiVO4 heterojunction was highest when prepared under a pH of 8.0. The initial rhodamine B in the solution (5 mg/L) was completely degraded within three hours. Recycling experiments verified the high stability of Bi2S3/BiVO4. The synthesis method proposed in this paper is expected to enable large-scale and practical use of Bi2S3/BiVO4.

Enhanced Photocatalytic Activity of NaBH4 Reduced BiFeO3 Nanoparticles for Rhodamine B Decolorization

“…This limits the practical application of TiO 2 as a photocatalyst. To make better use of solar energy that consists largely of visible light, it is essential to explore visible-light-driven photocatalysts [ 3 , 4 , 5 ].…”

Bismuth Sulfide Strongly Coupled to Functionalized MWNTs Hybrids with Improved Thermoelectric Properties

“…However, the peaks for the composite are shifted to slightly higher binding energy related to the pure Bi 2 S 3 , indicative of interfacial chemical interaction between the Bi 2 S 3 and f‐MWNT. [ 32 ] Further analysis shows that the Bi 4f 7/2 peak can be deconvoluted into two Gaussian components (Figure 4d–f). These components appear to be present in both the pure Bi 2 S 3 and the composites, but the relative intensities of the components differ across samples.…”

Visible‐Light‐Assisted Photocatalytic Degradation of Phenolic Compounds Using Bi2S3/Bi2W2O9 Heterostructure Materials as Photocatalyst

“…The bismuth tungstate material is a well explored n‐type semiconducting material whereas, Bi 2 S 3 exhibits p‐type semiconducting property . After contact between the two semiconducting materials, the equilibrium between the Fermi levels takes place leading to the realignment of the band structures.…”