Synthesis of graphitic carbon nitride-based photocatalysts for hydrogen evolution under visible light

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...
2
1
1
1

Citation Types

0
7
0

Year Published

2021
2021
2024
2024

Publication Types

Select...
7
1

Relationship

2
6

Authors

Journals

citations
Cited by 21 publications
(7 citation statements)
references
References 18 publications
0
7
0
Order By: Relevance
“…The lamellar structures loosely agglomerate between each other, resulting in microsized g-C3N4 particles of irregular shapes. The XRD pattern of the g-C3N4 is characterized by the dominant diffraction peak located at 2θ~27.5° and the second peak of lower intensity located at 2θ~13.1° [ 28 ]. The representative XRD patterns of the g-C3N4 produced from melamine (g-C3N4 (M)) and dicyandiamide (g-C3N4 (D)) are shown in Figure 5 c. The dominant diffraction peak can be assigned to the (002) plane and characterizes the distance between the parallel conjugated aromatic C-N 2D layers, whereas the second diffraction peak can be attributed to the (100) diffraction plane and characterizes the distance between the tri-s-triazine units within the 2D C-N layer.…”
Section: Properties Of G-c 3 Nmentioning
confidence: 99%
See 1 more Smart Citation
“…The lamellar structures loosely agglomerate between each other, resulting in microsized g-C3N4 particles of irregular shapes. The XRD pattern of the g-C3N4 is characterized by the dominant diffraction peak located at 2θ~27.5° and the second peak of lower intensity located at 2θ~13.1° [ 28 ]. The representative XRD patterns of the g-C3N4 produced from melamine (g-C3N4 (M)) and dicyandiamide (g-C3N4 (D)) are shown in Figure 5 c. The dominant diffraction peak can be assigned to the (002) plane and characterizes the distance between the parallel conjugated aromatic C-N 2D layers, whereas the second diffraction peak can be attributed to the (100) diffraction plane and characterizes the distance between the tri-s-triazine units within the 2D C-N layer.…”
Section: Properties Of G-c 3 Nmentioning
confidence: 99%
“…( c ) XRD patterns of g-C 3 N 4 (M) and g-C 3 N 4 (D) prepared from melamine and dicyandiamide, respectively. Reprinted with permission from [ 28 ], Copyright 2021, Elsevier. ( d ) UV-vis spectra of the g-C 3 N 4 and melon with the corresponding photographs of the powdery samples used for this measurement.…”
Section: Figurementioning
confidence: 99%
“…In general, platinization of the photocatalyst was carried out by the method described elsewhere. 35 The photocatalyst was impregnated by hexachloroplatinic acid solution (0.1 M); aer that the 2.5-fold excess of sodium borohydride was added. The mixture was stirred during 20 min, then the precipitate was collected, washed out by distilled water and dried at 50 C. The obtained samples were marked as Pt-yCd(1 À x)-P25, e.g.…”
Section: Photocatalyst Preparationmentioning
confidence: 99%
“…Melamine was chosen as a precursor. Usually, 2 g of the precursor was annealed in a ceramic crucible with a lid at 600 • C with a heating rate of 5 • C/min for 2 h [8]. The obtained g-C 3 N 4 was ground in a mortar to a yellow powder.…”
Section: Photocatalyst Synthesismentioning
confidence: 99%
“…These properties make g-C 3 N 4 an ideal semiconductor for photocatalytic hydrogen production, CO 2 reduction, and solar-cell applications [5][6][7]. However, quantum efficiency in the photocatalytic hydrogen production over pristine g-C 3 N 4 is quite low [8].…”
Section: Introductionmentioning
confidence: 99%