The Spread of Corrosion in Cast Iron and its Effect on the Life Cycle of Transportation Vehicles

Abstract

This article deals with the spread of corrosion in material at different exposure times, and its effect on the measured brittle fracture and notch impact strength under different temperature conditions. To assess the degradational effect of corrosion on the material characteristics represented by the measured impact strength, we conducted a fractographic analysis of fracture surfaces, the aim of which was to evaluate the spread of corrosion in the material. In the first part of the experiment, two corrosion tests are simulated with a duration time of 432 and 648 hours, to compare the degradation effect of corrosion on the notch impact strength, depending on the duration of the corrosion tests. The following part shows the results of the impact bending test, where the experiment was conducted in an area of reduced and increased temperatures. The final part summarizes the results of the fractographic analysis of sample fracture surfaces from the impact bending tests. Based on the measured the length of the corrosion cracks, we analyzed the sample at the notch and from the material surface after the impact bending test.

Cargo Securing - Comparison of Different Quality Roads

“…Changes in the Czech transport system, especially after 1989, are evident. It is not only infrastructure,butalsomeansoftransportandincreasedtransportcapacity.The poorcondition ofmanytransportroutesinthe CzechRepubliccanresultnotonlyinincreasedrepaircostsand shortenedvehiclelife-cycles (Binar et al,2017),butalsoinincreasedaccidentrates,whichcan bediscussedinaneconomiccontext (Vlkovský,VeselíkandGrzesica,2018). Furtherresearchwillfocusonthe analysisofcasestudiesforotherrelevantvehicletypes(e.g.…”

Investigation of material properties using acoustic emission

“…For the purpose, in this case, the NWMS nonlinear ultrasonic method measurements were used several times during the corrosion test. [2,3] 1. Experiment 1.1.…”