Transitions solide-solide dans le systeme CaO-Na2O-P2O5 sous-systeme Ca3(PO4)2-CaNaPO4 Etude par diffraction de rayons X à température variable

Abstract

The phase diagram of solid-solid equilibria in the system Ca3(PO4}-CaNaPO 4 has been studied by thermal analysis. The results are confirmed by X-ray diffraction at different temperatures. This study was limited to that of mixtures in a temperature range determined by previous results. The pcesent work confirms the existence of two metastable diagrams which are superimposed on the stable diagram.The experimental conditions leading to the formation of the metastable phases on cooling (cooling rate and highest temperature reached before cooling) and to the different types of metastability were determined from the differential X-ray diffraction spectra.L'dtablissement du diagramme de phase des dquilibres solide-solide du syst~me Ca3(PO4)2-CaNaPO4 par analyses thermiques directe et diffdrentielle coupldes a fait I'objet d'une premiere sdrie d'~tudes [1][2][3].Diff~rents diagrammes de phase avaient auparavant dtd proposals pour ce syst~me [4,5]. Ces diffdrences, portant sur les limites du domaine d'existence d'une phase non stoechiom6trique (phase A) stable ~ haute temp6rature, ont pu ~tre expliqu6es par la mise en 6vidence de deux diagrammes mdtastables pouvant ~tre d~crits au refroidissement.Les rdsultats d'analyse thermique au chauffage ont permis de tracer le diagramme des dquilibres stables du syst~me, prdsent~ sur la figure 1. Dans ca diagramme, la phase A se forme b 980 ~ pour une composition en poids de CaNaPO 4 de 50% environ, selon la rdaction eutectoi'de: /~Ca3(PO4)2 + o~,aNaPO4 -* A.