Abstract-EuCARD-2 is a project supported by FP7-European Commission that includes, inter alia, a work-package (WP10) called "Future Magnets". This project is part of the long term development that CERN is launching to explore magnet technology at 16 T to 20 T dipole operating field, within the scope of a study on Future Circular Colliders. The EuCARD2 collaboration is closely liaising with similar programs for high field accelerator magnets in the USA and Japan. The main focus of EuCARD2 WP10 is the development of a 10 kA-class superconducting, high current density cable suitable for accelerator magnets, The cable will be used to wind a stand-alone magnet 500 mm long and with an aperture of 40 mm. This magnet should yield 5 T, when stand-alone, and will enable to reach a 15 to 18 T dipole field by placing it in a large bore background dipole of 12-15 T. REBCO based Roebel cables is the baseline. Various magnet configurations with HTS tapes are under investigation and also use of Bi-2212 round wire based cables is considered. The paper presents the structure of the collaboration and describes the main choices made in the first year of the program, which has a breadth of five to six years of which four are covered by the FP7 frame.

A transport current distribution over a wide superconducting sheet is shown to strongly change in the presence of bulk magnetic screens of a soft magnet with a high permeability. Depending on the geometry, the effect may drastically suppress or protect the Meissner state of the sheet through the enhancement or suppression of the edge barrier critical current. The total transport current in the magnetically screened Meissner state is expected to compete with the critical current of the flux-filled sheet only for samples whose critical current is initially essentially controlled by the edge barrier effect.

An inductive methodology simultaneously enabling the determination of grain- and intergrain critical current densities of YBa2Cu3O7−x coated conductors is developed. This noninvasive method is based on the identification of a clear peak in the reverse branch of the magnetization loop at a positive magnetic field, as a signature of the electromagnetic granularity inherent to these materials. A quantitative evaluation of the return magnetic field at the grain boundaries allows us to understand the existence of this magnetization peak and quantify the grain critical current density. This methodology is envisaged to sort out granularity effects from vortex pinning effects on coated conductors.

The superconductor industry is demanding new methodologies to manufacture km-long, high quality coated conductors at high growth rates, using cost-effective, scalable processes. We report on the fabrication by an all-chemical deposition method of highly textured, thick (0.9 µm) inkjet-printed YBCO films, using a Ce 0.9 Zr 0.1 O 2 (CZO) capping layer deposited by MOD, on top of robust, buffered ABAD YSZ/SS substrates. Thinner, 0.25 µm spin-coated YBCO films were also analyzed for comparison. The structural study performed by x-ray diffraction, optical, AFM, SEM and TEM microscopy demonstrates the success of the capping layer for enhancing the planarity of the as-received tape and obtaining highly homogeneous and well-textured YBCO films. DC magnetometry granularity analysis was used to determine the mean superconducting grain diameter, ∼2.5 µm, and the intra-and intergranular critical current densities of the coated conductors (CCs). For the thin, spin-coated sample, high self-field intragrain critical currents were measured (J G c = 40, 3.3 MA cm −2 at 5, 77 K). For the thick, inkjet-printed tape J G c was reduced by ∼30%, but, notably, the percolative critical current, J GB c = 12.5 MA cm −2 , was only ∼10% smaller at 5 K, thanks to good preservation of the texture. At 77 K, J GB c = 1.3 MA cm −2 was achieved, implying a critical current of I c = 117 A/cm-width. AC susceptibility measurements allowed us to demonstrate the high homogeneity of the fabricated CCs, and investigate the magnetic vortex-pinning phase diagram. Remarkably, the thick, inkjet-printed sample showed comparable irreversibility line (IL) and activation energy for thermal depinning, U e (H), to the thin sample. The present results open new perspectives for the fabrication of high quality-to-cost ratio, all-chemical CCs with yet higher I c values by inkjet printing multideposition of thicker YBCO layers.