Embedded GaSb nanofibers with an intact surface layer are formed by high‐energy ion irradiation of bulk single‐crystal GaSb (see image). Distinct regimes are present within the fiber layer and the effects of varying implant parameters on the fiber regimes are reported. A growth model for nanofibers is presented, as well as a model for the dose‐dependant removal of the surface cover.
Amorphous GaSb nanofibers were obtained by ion beam irradiation of bulk GaSb single-crystal wafers, resulting in fibers with diameters of ~20 nm. The Raman spectra and photoluminescence (PL) of the ion irradiation-induced nanofibers before and after annealing were studied. Results show that the Raman intensity of the GaSb LO phonon mode decreased after ion beam irradiation as a result of the formation of the amorphous nanofibers. A new mode is observed at ~155 cm-1 both from the unannealed and annealed GaSb nanofiber samples related to the A1g mode of Sb–Sb bond vibration. Room temperature PL measurements of the annealed nanofibers present a wide feature band at ~1.4–1.6 eV. The room temperature PL properties of the irradiated samples presents a large blue shift compared to bulk GaSb. Annealed nanofibers and annealed nanofibers with Au nanodots present two different PL peaks (400 and 540 nm), both of which may originate from Ga or O vacancies in GaO. The enhanced PL and new band characteristics in nanostructured GaSb suggest that the nanostructured fibers may have unique applications in optoelectronic devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.