In this paper, the room temperature mechanical properties, as well as the microstructure of HK 30 Nb steel, were tested in the initial as-cast and solution annealed condition. Results show that tensile properties after the solution annealing have a slightly lower value than as-cast samples. Microstructural analysis of samples after solution annealing showed dissolution of primary carbides present in the initial as-cast condition. The morphology and composition of carbides were changed during a solution annealing. Analysis of microstructure was done by optical microscopy (OM) and scanning electron microscope (SEM), whereas hardness and tensile tests were performed for characterization of mechanical properties.