The aim of this study was to evaluate the efficacy of different surface conditioning methods on the microtensile bond strength of a restorative composite repair in three types of dental ceramics: lithium disilicate-reinforced, leucite-reinforced and feldspathic. Twelve blocks were sintered for each type of ceramic (n=3) and stored for 3 months in distilled water at 37 °C. The bonding surface of ceramics was abraded with 600-grit SiC paper. Surface treatments for each ceramic were: GC (control)-none; GDB-diamond bur #30 µm; GHF-hydrofluoric acid (10%); GT-tribochemical silica coating (45-μm size particles). Treatments were followed by cleaning with phosphoric acid 37% for 20 s + silane + adhesive. The composite resin was used as restorative material. After repair, samples were subjected to thermocycled ageing (10,000 cycles between 5 °C and 55 °C for 30 s). Thereafter, the samples were sectioned into 1.0 mm 2 sticks and tested for microtensile bond strength with 0.5 mm/min crosshead speed. Data were compared by two-way ANOVA and Tukey's test (α=0.05). The superficial wear with diamond bur proved to be suitable for feldspathic porcelain and for leucite-reinforced glass ceramic while hydrofluoric acid-etching is indicated for repairs in lithium disilicate-reinforced ceramic; tribochemical silica coating is applicable to leucite-reinforced ceramic. Predominance of adhesive failures was observed (>85% in all groups). In conclusion, the success of surface treatments depends on the type of ceramic to be repaired.
This study evaluated the influence of retorque on loosening torque (Lt) of prosthetic screws in implant-supported dentures with different fit levels. Ten mandibular implant-supported dentures were fabricated and then 20 cast models were then prepared using prosthetic structures to create 2 fit levels: passive fit (Pf) and misfit (Mf). Two tightening techniques were also evaluated: initial torque only (T1); and initial torque and retorque after 10 min (T2). Gold or titanium screws were used, resulting in 4 groups to each one: Pf/T1, Pf/T2, Mf/T1, Mf/T2. The Lt was measured 24 h after the tightening torque using digital torque meter. Data were analyzed statistically by two-way ANOVA and Tukey's test (α=0.05), separately for each screw material. For titanium screws, no significant difference (p>0.05) was found between Pf/T1 and Pf/T2, or between Pf/T2 and Mf/T2. However, statistically significant difference (p<0.05) was found between Pf/T1 and Mf/T1, and between Mf/T1 and Mf/T2. Mf reduced the Lt using T1, while and T2 increased the Lt for Mf. Retorque and fit were shown to have no significant influence on the Lt of the gold screws. Retorque application made insignificant the misfit effect on the Lt of the titanium screws, suggesting that this procedure should be performed routinely during the screw tightening in multi-unit dentures.
According to finite element analysis, the zirconia ceramic post created higher stress levels in the post and slightly less in dentin compared with glass fiber posts. Resin cement with a high elastic modulus created higher stress levels in the cement layer. The different film thicknesses of cement did not create significant changes in stress levels.
SUMMARYThe current study evaluated the influence of two endodontic post systems and the elastic modulus and film thickness of resin cement on stress distribution in a maxillary central incisor (MCI) restored with direct resin composite using finite element analysis (FEA). A three-dimensional model of an MCI with a coronary fracture and supporting structures was performed. A static chewing pressure of 2.16 N/mm 2 was applied to two areas on the palatal surface of the composite restoration. Zirconia ceramic (ZC) and glass fiber (GF) posts were considered. The stress distribution was analyzed in the post, dentin and cement layer when ZC and GF posts were fixed to the root canals using resin cements of different elastic moduli (7.0 and 18.6 GPa) and different layer thicknesses (70 and 200 µm). The different post materials presented a significant influence on stress distribution with lesser stress concentration when using the GF post. The higher elastic modulus cement created higher stress levels within itself. The cement thicknesses did not present significant changes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.