Objective:The objective of this study was to compare the torque and detorque values of screw intermediates of external hexagon, internal hexagon, and Morse taper implants in single restorations before and after mechanical cycling.Materials and Methods:The study sample was divided into three groups (n = 10) as follows: group EH – external hexagon implant, group IH – internal hexagon implant, and group MT – Morse taper implant. Universal abutments were screwed on the implants, and metal crowns were cemented onto the abutment. The samples were submitted to a mechanical testing of 1 million cycles, with a frequency of 8 cycles per second under a 400 N load. The application and registration of the screw torque (T0) and detorque (T1) values of the intermediate were performed before and after the test. The results were statistically evaluated by analysis of variance (ANOVA) and Tukey's test (α = 0.05).Results:There was no difference between the values of T0 and T1 in the intra-group samples. However, the inter-group difference in T0 between the EH (12.8 N cm) and MT (18.6 N cm) groups and in T1 between the EH (10.4 N cm) and IH (13.8 N cm), EH and MT (19.4 N cm), and MT and IH (P = 0.001) groups were significant. The MT group showed a lower variation of T0 and T1.Conclusion:The internal implants, particularly MT, showed better stability in these cases when used for single restorations.

PURPOSEThis study evaluated the dimensional stability of a complete-arch prosthesis processed by conventional method in water bath or microwave energy and polymerized by two different curing cycles.MATERIALS AND METHODSForty maxillary complete-arch prostheses were randomly divided into four groups (n = 10): MW1 - acrylic resin cured by one microwave cycle; MW2 - acrylic resin cured by two microwave cycles: WB1 - conventional acrylic resin polymerized using one curing cycle in a water bath; WB2 - conventional acrylic resin polymerized using two curing cycles in a water bath. For evaluation of dimensional stability, occlusal vertical dimension (OVD) and area of contact points were measured in two different measurement times: before and after the polymerization method. A digital caliper was used for OVD measurement. Occlusal contact registration strips were used between maxillary and mandibular dentures to measure the contact points. The images were measured using the software IpWin32, and the differences before and after the polymerization methods were calculated. The data were statistically analyzed using the one-way ANOVA and Tukey test (α = .05).RESULTShe results demonstrated significant statistical differences for OVD between different measurement times for all groups. MW1 presented the highest OVD values, while WB2 had the lowest OVD values (P<.05). No statistical differences were found for area of contact points among the groups (P=.7150).CONCLUSIONThe conventional acrylic resin polymerized using two curing cycles in a water bath led to less difference in OVD of complete-arch prosthesis.

Avaliação da alteração dimensional da base de prova permanente da prótese total de resina acrílica ativada termicamente, processada em forno microondas, por meio da imagem digital

Objetivos: O objetivo deste trabalho foi avaliar os efeitos da administração sistêmica do chumbo, preparado de acordo com a farmacotécnica homeopática Plumbum metallicum 30CH, na reparação óssea. Material e métodos: foram utilizados trinta ratos machos com três meses de idade, nos quais foram confeccionados defeitos cirúrgicos trans-ósseos com broca de aço nº 06 na região do ângulo da mandíbula do lado direito, sem utilização de barreira mecânica. Cada animal do grupo experimental recebeu três gotas diárias de Plumbum metallicum 30CH acrescidas à mamadeira de água. Os animais do grupo controle receberam apenas água. Três animais foram sacrificados nos seguintes períodos experimentais: um, sete, 14, 21 e 28 dias após a cirurgia. Após o sacrifício, as mandíbulas foram removidas, descalcificadas e submetidas ao preparo histológico de rotina. Foram submetidas a cortes semi-seriados e coradas pelos métodos de hematoxilina-eosina e tricômico de Masson para análise histológica em microscópio de luz. Resultados: os resultados obtidos neste trabalho mostraram que o medicamento foi eficiente na estimulação da reparação óssea. A análise histológica qualitativa mostrou evidência de efeito favorável do Plumbum mettalicum 30 CH. Apesar da interferência do tecido muscular, os animais mostraram, já a partir do período de 14 dias, neoformação óssea em praticamente toda a extensão do defeito. Conclusão: a utilização do Plumbum metallicum 30CH favoreceu a reparação de defeitos ósseos em mandíbula de ratos machos, sem a utilização de barreira mecânica.

A educação a distância tem crescido no ensino superior, para conhecer de que forma acontece o ensino híbrido é necessário compreender as dificuldades, os avanços e os desafios apresentados pelos seus envolvidos. Este artigo tem como objetivo compreender os critérios utilizados pelos professores de disciplinas presenciais e online e nas avaliações acadêmicas durante o processo educativo semestral. Pode-se observar que os professores usam critérios diferenciados para avaliar seus alunos nas diferentes modalidades, porém é perceptível que o ensino híbrido tem sido mais eficiente que o ensino totalmente a distância. O processo educativo deve partir de ambas as partes uma vez que a relação entre o professor e aluno, por meio do ensino EAD, muitas vezes só acontece por meio do computador já que o professor atua como mediador do conhecimento.