Rice husk (RH), an abundant agricultural residue, was reacted with 2-bromoisobutyryl bromide, to convert it to a heterogeneous polyfunctional macroinitiator for Atom Transfer Radical Polymerization (ATRP). The number of active sites placed on the RH surface was small, but they were ATRP active. Non-polar methyl methacrylate (MMA) and polar acrylonitrile (AN) were polymerized from the RH, and a sequential monomer addition was used to prepare an amphiphilic PMMA-b-PAN copolymer on RH surface. FTIR qualitatively confirmed the grafting. Gravimetric and XPS analysis of the different RH surface compositions indicated thin layers of oligomeric PMMA, PAN, and PMMA-b-PAN. The modified surfaces were mapped by nanomechanical AFM to measure surface roughness, and adhesion and moduli using the Derjaguin-Muller-Toropov model. RH grafted with MMA possessed a roughness value of 7.92, and a hard and weakly adhering surface (13.1 GPa and 16.7 nN respectively) while RH grafted with AN yielded a roughness value of 29 with hardness and adhesion values of 4.0 GPa and 23.5 nN. The PMMA-b-PAN modification afforded a surface with a roughness value of 51.5 nm, with hardness and adhesion values of 3.0 GPa and .75.3 nN.

In spite of extensive studies on the preparation and characterization of nanocomposite materials, the correlation of their properties at the nanoscale with those in bulk is a relatively unexplored area. This is of great importance, especially for materials with potential biomedical applications, where surface properties are as important in determining their applicability as bulk characteristics. In this study, the nanomechanical characteristics of thin poly(vinyl alcohol) (PVOH)-poly(acrylic acid) (PAA)-cellulose nanocrystal (CNC) membranes were studied using the nanoindentation module in an atomic force microscope (AFM) and the properties were compared with the macro-scale properties obtained by tensile tests. In general, the elastic properties measured by nanoindentation followed the same trend as macro-scale tensile tests except for the PVOH 85-PAA 0-CNC 15 sample. In comparison to the macro-scale elastic properties, the measured elastic moduli with AFM were higher. Macro-scale tensile test results indicated that, in the presence of PAA, incorporation of CNCs up to 20 wt% improved the elastic modulus of PVOH, but when no PAA was added, increasing the CNC content above 10 wt% resulted in their agglomeration and degradation in mechanical properties of PVOH. The discrepancy between macro-scale tensile tests and nanoindentation in the PVOH 85-PAA 0-CNC 15 sample was correlated to the high degree of inhomogeneity of CNC dispersion in the matrix. It was found that the composites reinforced with cellulose nanocrystals had smaller indentation imprints and the pile-up effect increased with the increase of cellulose nanocrystal content.