Nano-structured calcium silicate (NCS), a highly porous material synthesized by controlled precipitation from geothermal fluids or sodium silicate solution, was developed as filler for use in paper manufacture. NCS has been shown to chemisorb orthophosphate from an aqueous solution probably obeying a Freundlich isotherm with high selectivity compared to other common environmental anions. Microanalysis of the products of chemisorption indicated there was significant change from the porous and nano-structured morphology of pristine NCS to fibrous and crystalline morphologies and non-porous detritus. X-ray diffraction analysis of the crystalline products showed it to be brushite, CaHPO42H2O, while the largely X-ray amorphous component was a mixture of calcium phosphates. A two-step mechanism was proposed for the chemisorption of phosphate from an aqueous solution by NCS. The first step, which was highly dependent on pH, was thought to be desorption of hydroxide ions from the NCS surface. This was kinetically favoured at lower initial pH, where the predominant form of phosphate present was H2PO(-)4, and led to decreased phosphorus uptake with increasing pH. The second step was thought to be a continuing chemisorption process after stabilization of the pH-value. The formation of brushite as the primary chemisorption product was found to be consistent with the proposed mechanism.

No abstract

Up to 7.4% (w/w) of the sulfonated polyaniline, poly(2-methoxyaniline-5-sulfonic acid) (PMAS) can be absorbed onto nanostructured calcium silicates. Spectroscopic and leaching studies on the novel PMAS-silicate nanocomposites obtained indicate that attachment of the PMAS occurs via electrostatic binding of PMAS sulfonate groups to Ca2+ sites on the silicates. The surface area and pore volume of the nanocomposites are comparable to those of pure silicate and increase the surface area of the PMAS polymer by several orders of magnitude. The PMAS emeraldine salt in the nanocomposites retains its chemical reactivity, being readily oxidised and reduced to its pernigraniline and leucoemeraldine forms, respectively. The conductivity of the composite is comparable to that of the pure PMAS, several orders of magnitude higher than that of dried nanostructured calcium silicate.