A non weldable nickel-based superalloy was fabricated by powder bed-based selective electron beam melting (S-EBM). The as-built samples exhibit a heterogeneous microstructure along the build direction. A gradient of columnar grain size as well as a significant gradient in the γ' precipitate size were found along the build direction. Microstructural defects such as gas porosity inherited from the powders, shrinkage pores and cracks inherited from the S-EBM process were identified. The origins of those defects are discussed with a particular emphasis on crack formation. Cracks were consistently found to propagate intergranular and the effect of crystallographic misorientation on the cracking behavior was investigated. A clear correlation was identified between cracks and high angle grain boundaries (HAGB). The cracks were classified as hot cracks based on the observation of the fracture surface of microtensile specimens machined from as-built S-EBM samples. The conditions required to trigger hot cracking, namely, presence of a liquid film during the last stage of solidification and thermal stresses are discussed within the framework of additive manufacturing. Understanding the cracking mechanism enables to provide guidelines to obtain crack-free specimens of non-weldable Ni-based superalloys produced by S-EBM.
Additive manufacturing processes, used for more than 25 years, are no longer confined to rapid prototyping applications. Mostly used nowadays in niche markets (medical applications, aerospace. . . ) to manufacture metallic parts, they should provide improvements in terms of time-to-market, ecological impact and design compared to traditional industrial processes. Current metallic additive manufacturing studied in this paper are Selective Laser Sintering, Direct Metal Laser Sintering, Selective Laser Melting, Electron Beam Melting and Direct Metal Deposition. The performances of these processes are investigated through criteria derived from the time cost quality triangle and some prospects concerning these processes are given.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.