Dispersion of carbon nanotubes and carbon nanofibers is a crucial processing step in the production of polymer-based nanocomposites and poses a great challenge due to the tendency of these nanofillers to agglomerate. Besides the well-established three-roll mill, the ultrasonic dispersion process is one of the most often used methods. It is fast, easy to implement, and obtains considerably good results. Nevertheless, damage to the nanofibers due to cavitation may lead to shortening and changes in the surface of the nanofillers. The proper application of the sonicator to limit damage and at the same time enable high dispersion quality needs dedicated knowledge of the damage mechanisms and characterization methods for monitoring nano-particles during and after sonication. This study gives an overview of these methods and indicates parameters to be considered in this respect. Sonication energy rather than sonication time is a key factor to control shortening. It seems likely that lower powers that are induced by a broader tip or plate sonicators at a longer running time would allow for proper dispersions, while minimizing damage.
Nano-reinforcements in carbon fibre-reinforced polymer (CFRP) have proven to enhance the mechanical properties considering quasi-static, as well as fatigue load and, are a promising option with regard to CFRP performance optimisation. While general knowledge about the nanofiller content and its influence in CFRP is well documented, the use of alignment techniques for a specific orientation of the nano-reinforcements is still insufficiently studied. In this work, the influence of oriented carbon nanofibres (CNF) on the mechanical properties of bidirectional CFRP is investigated. CFRP was produced CNF-reinforced with and without orientation using a hot press, where an electric field was applied during curing. The laminates were characterised with respect to dispersion quality, pore volume, quasi-static properties (tensile and bending tests) and dynamic properties (fatigue tests). Electrical resistance measurement was applied together with digital image correlation and in situ computed tomography to generate knowledge about the fatigue-related damage evolution and evaluate the sensors for viable use of condition monitoring. Results show that the orientation of CNF has a significant impact on both quasi-static and fatigue properties, increasing the strength while reducing and slowing down the introduced damage. Orientation of nanofillers thus shows large optimization potential of mechanical properties of CFRP components.
Dispersion of carbon nanotubes and carbon nanofibers is a crucial processing step in the production of polymer-based nanocomposites and poses a great challenge due to the tendency of nanofillers to agglomerate. One of the most effective methods for dispersion is the use of a three-roll mill, which is a well-established method and results in agglomerates below 5 µm. Nevertheless, this process is time-consuming and thus a limiting factor for industrial applications. Our aim was to establish an easy and efficient ultrasonic dispersion process, characterize the dispersion parameters, and compare both methods, ultrasonication and the three-roll mill. We applied rheological tests and analyzed the agglomerate sizes by an image fit of the microscopy images. All these analyses combined deliver a valuable set of information about the dispersion’s quality and, therefore, allows the improvement and further adaptation of the dispersion process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.