The new era of spintronics promises the development of nanodevices, where the electron spin will be used to store information and charge currents will be replaced by spin currents. For this, ferromagnetic semiconductors at room temperature are needed. We report on significant room-temperature spin polarization of EuS in Co/EuS multilayers recorded by x-ray magnetic circular dichroism (XMCD). The films were found to contain a mixture of divalent and trivalent europium, but only Eu++ is responsible for the ferromagnetic behavior of EuS. The magnetic XMCD signal of Eu at room temperature could unambiguously be assigned to magnetic ordering of EuS and was found to be only one order of magnitude smaller than that at 2.5 K. The room temperature magnetic moment of EuS is as large as the one of bulk ferromagnetic Ni. Our findings pave the path for fabrication of room–temperature spintronic devices using spin polarized EuS layers.

Ultraviolet-visible absorption spectra of nanoscaled EuS thin films reveal a blue shift of the energy between the top-valence and bottom-conduction bands. This band-gap tuning changes smoothly with decreasing film thickness and becomes significant below the exciton Bohr diameter ∼3.5 nm indicating strong quantum confinement effects. The results are reproduced in the framework of the potential morphing method in Hartree Fock approximation. The large values of the effective mass of the holes, due to localization of the EuS f-states, limit the blue shift to about 0.35 eV. This controllable band-gap tuning of magnetic semiconductor EuS renders it useful for merging spintronics and optoelectronics.

Two identical Co/EuS and Fe/EuS multilayers of six periods each and with individual layers of about 4 nm thick are grown by e-beam evaporation under ultrahigh vacuum conditions. The films show polycrystalline structure with a grain size limited by the individual layer thickness. Both multilayers consist of almost continuous layers with some roughness. The surface peak-to-peak roughness is about 4–5 nm. Magnetization measurements and calculations of the loops based on a Stoner–Wohlfarth-like model allow us to determine the direct antiferromagnetic exchange coupling constant between the 3d metal and EuS at 5 K. Both samples show strong enhancement of the Curie temperature of EuS up to at least 50 K with a EuS magnetization tail, which persists up to about 100 K. The J = 7/2 character of the EuS layers is shown to be responsible for the large Curie temperature enhancement.