1-Benzyl-3-methyl-imidazolium hexafluoroantimonate (BMH) was newly synthesized and characterized with FT-IR, 1H-NMR. We synthesized catalysts fulfill requirements for a rapid cure at a moderately elevated temperature in curing the epoxy resin for neat diglycidyl ether bisphenol A (DGBEA). The cure behavior of this resin was investigated at elevated temperature and cure temperature in the presence of 0.5, 1.0, 2.0 wt% of 1-benzyl-3-methyl-imidazolium hexafluoroantimonate (BMH) by mean of differential scanning calorimeter (DSC). Chemical conversion as function of temperature and amount of BMH (0.5, 1.0, 2.0 wt%) were determined from DSC. It was found that BMH were superior latent thermal catalyst for catinonic curing which have a good thermal stability.

The epoxy composites with high thermal conductivity for metal-core printed circuit board (MCPCB) can be prepared by varnish coating and a hot press method. Alumina filler of plate-like shape was used as primary micro-filler, while plate-like alumina filler, h-BN, a-BN and s-BN filler were used for blending into the plate-like alumina filler as the secondary filler. Results showed that the secondary fillers a-BN and s-BN loaded epoxy composites have higher thermal conductivity than alumina filler single-loaded composites. Also, BN filler has high thermal conductivity, but h-BN filled epoxy composite has lower thermal conductivity than alumina filled epoxy composite. The decrease of voids in epoxy composite are very important, and the filler shape and surface modification is also necessary to achieve high thermal conductivity in epoxy composite for MCPCB