We report on the material, electrical, and optical properties of metal–semiconductor–metal ultraviolet photodetectors fabricated on single-crystal GaN, with active layers of 1.5 and 4.0 μm thickness. We have modeled current transport in the 1.5 μm devices using thermionic field emission theory, and in the 4.0 μm devices using thermionic emission theory. We have obtained a good fit to the experimental data. Upon repeated field stressing of the 1.5 μm devices, there is a degradation in the current–voltage (I–V) characteristics that is trap related. We hypothesize that traps in the GaN are related to a combination of surface defects (possibly threading dislocations), and deep-level bulk states that are within a tunneling distance of the interface. A simple qualitative model is presented based on experimental results. For devices fabricated on wafers with very low background free electron concentrations, there is a characteristic “punch-through” voltage, which we attribute to the interaction of the depletion region with the underlying low-temperature buffer layer. We also report GaN metal–semiconductor–metal photodetectors with high quantum efficiencies (∼50%) in the absence of internal gain. These photodetectors have a flat responsivity above the band gap (measured at ∼0.15 A/W) with a sharp, visible-blind cutoff at the band edge. There is no discernible responsivity for photons below the band-gap energy. We also obtained record low dark current of ∼800 fA at −10 V reverse bias. The dark current and ultraviolet photoresponse I–V curves are very flat out to VR>−25 V, and do not show evidence of trap-related degradation, or punch-through effects.
We report the electrical and optical characteristics of avalanche photodiodes fabricated in GaN grown by metalorganic chemical vapor deposition. The current–voltage characteristics indicate a multiplication of >25. Experiment indicates and simulation verifies that the magnitude of the electric field at the onset of avalanche gain is ⩾3 MV/cm. Small-area devices exhibit stable gain with no evidence of microplasmas.
A SiC p-i-n junction betavoltaic was fabricated, and electrical power output under irradiation from an 8.5GBq P33 source was monitored over a period of four half-lives of the radioisotope. The open-circuit voltage (VOC) of the device was 2.04±0.02V, and the peak power (Pout) was 0.58±0.02μW (2.1±0.2μW∕cm2) at 1.60V. The conversion efficiency (ηconv) was 4.5%±0.3% and the normalized power output indicates no device degradation over more than 3months (four half-lives of the source).
Articles you may be interested inPerformance improvement of GaN-based ultraviolet metal-semiconductor-metal photodetectors using chlorination surface treatment J. Vac. Sci. Technol. B 30, 031211 (2012); 10.1116/1.4711215 Effect of asymmetric Schottky barrier on GaN-based metal-semiconductor-metal ultraviolet detector Appl. Phys. Lett. 99, 261102 (2011); 10.1063/1.3672030 Influence of threading dislocations on GaN-based metal-semiconductor-metal ultraviolet photodetectors Appl. Phys. Lett. 98, 011108 (2011); 10.1063/1.3536480 GaN metal-semiconductor-metal ultraviolet photodetector with IrO 2 Schottky contact Appl. Phys. Lett. 81, 4655 (2002); 10.1063/1.1524035High-speed, low-noise metal-semiconductor-metal ultraviolet photodetectors based on GaN
Articles you may be interested inComparison of hole traps in n-GaN grown by hydride vapor phase epitaxy, metal organic chemical vapor deposition, and epitaxial lateral overgrowth
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.