This study evaluated the infl uence of beverages and brushing on the surface roughness(SR) and color change(∆E) of a composite resin. For this, 120-disks(10 mm×2 mm) of composite resin(Filtek-Z250) were prepared and polished. Initials SR(Ra-μm) and color(CIELabsystem) were measured with rugosimeter and spectrophotometer; specimens were divided into four groups(red wine, soft drink, sugar cane spirit, or artifi cial saliva=control) and three subgroups(without brushing; brushed with Colgate or with Close-Up). Specimens were immersed in the beverage 5×/day, for 5', over 30 day, being two subgroups brushed(120 strokes/day). Color was measured at 15th day, 30th day and after repolishment; SR at 30th day. ∆E-values were statistically different after immersion in the beverages(p<0.05). Red wine promoted the highest alteration, followed by soft drink=sugar cane spirit and fi nally saliva. At 30th day, specimens exhibited ∆E higher than 15th day; after repolishing, ∆E was similar to 15th day. Beverages and brushing negatively infl uenced the SR. Therefore, ∆E and SR can be infl uenced by beverages and brushing.

The aim of the study was to evaluate mechanical behavior of implants inserted in three substrates, by measuring the pullout strength and the relative stiffness. 32 implants (Master Porous-Conexao, cylindrical, external hexagon, and surface treatment) were divided into 4 groups (n = 8): pig rib bone, polyurethane Synbone, polyurethane Nacional 40 PCF, and pinus wood. Implants were installed with the exact distance of 5 mm of another implant. The insertion torque (N·cm) was quantified using the digital Kratos torque meter and the pullout test (N) was performed by an axial traction force toward the long axis of the implant (2 min/mm) through mount implant devices attached to a piece adapted to a load cell of 200 Kg of a universal testing machine (Emic DL10000). Data of insertion torque and maximum pullout force were submitted to one-way ANOVA and Bonferroni tests (α = 0.05). Polyurethane Nacional 40 PCF and pinus wood showed the highest values of insertion torque and pullout force, with significant statistical difference (P < 0.05) with other groups. The analysis showed stiffness materials with the highest values for primary stability.

The study shows the influence of different implant macro-geometries and densities of substrates on primary stability.

Dental caries is still the most prevalent chronic disease affecting human populations. Among the preventive treatments performed, it has been reported that laser irradiation combined with topical fluoride can induce an even greater increase in enamel caries resistance. The aim of this study was to evaluate the Nd:YAG laser, with or without fluoride, in occlusal caries prevention of the primary dentition. A double-blind split-mouth study design was used. Fifty-two children with high caries risk (7.6 ± 1.4 years) were selected and received the following: G1--the first molar was a negative control, and the second received a resin sealant; G2--the first molar was a negative control, and the second received laser irradiation (50 mJ, 10 Hz, 0.5 W); G3--the first molar received only acidulate phosphate fluoride (APF), and the second received APF + laser; G4--fisrt molar received only fluoride varnish, and the second received fluoride varnish + laser. Patients were followed up to 12 months to evaluate the presence of white-spot lesions and/or caries cavities by three calibrated observers. Thirty-five patients completed the study. Significant differences were found between the treatment and control groups (p < 0.05). The laser-alone and resin sealant resulted in statistically lower caries formation than the negative control group (p < 0.05). Nd:YAG laser irradiation in primary teeth effectively prevented occlusal caries in pits and fissures when used alone with lower energy over a 1-year period.

The objective of this study was to evaluate the effects of chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser irradiation on the acid resistance of dental enamel. Forty human enamel samples were divided into four groups. They were manually irradiated with an Er,Cr:YSGG laser device (λ = 2.78 µm, 20 Hz, 20 s), in a scanning mode, with and without water cooling, according to the following parameters: Group 1: 0.25 W, 62.5 J/cm(2), no water cooling; group 2: 0.25 W, 62.5 J/cm(2), 5.0 ml/min; group 3: 0.5 W, 125 J/cm(2), no water cooling; group 4: 0.5 W, 125 J/cm(2), 5.0 ml/min. No airflow was used. Afterwards, the samples were submitted to an acid challenge and assessed by cross-sectional Knoop microhardness at different depths (20, 40, 60, 80, and 100 µm) from the outer enamel surface. Average values were obtained for both irradiated and control areas in each sample and they were compared to obtain a percentage of microhardness increase. Data were analyzed by analysis of variance and Fisher's exact test (α = 5%). The percentage of microhardness increase observed in group 1 (+23.58%) was similar to group 3 (+19.12%), but higher than groups 2 (+3.61%) and 4 (10.9%) (p < 0.05). The comparison of the depths showed that the Er,Cr:YSGG laser acted in the superficial layers of the dental enamel. The findings of the present study suggest that the energy densities of 62.5 and 125 J/cm(2) were capable of increasing the acid resistance of human enamel. The presence of water during irradiation makes it difficult to obtain an enamel surface more resistant to acids.