The melting and crystallization behaviour of undrawn poly(ethy1ene terephthalate)nylon 6 biconstituent fibers (BCF) have been investigated by DSC measurements. A decrease of the internal AT between the temperature of the glass transition and the temperature of the cold crystallization has been found. Changes of the temperature of the melt crystallization of the two components depending on the blend ratios (e. g. the phase morphology) have been also observed. These effects have been explained by an interface physical interaction which changes the degree of order of the molecules inside the phases. A relation between the decrease in AT of the PETP component and the maximum draw ratio A , , , , = of the BCF has been established. It is supposed that the change in AT causes the occurrence of local tensions and the initial formation of microcracks in the PETP phase which lead to a decrease of La. ZUSAMMENFASSUNG:Das Schmelz-und Kristallisationsverhalten von unverstreckten Polyethylenterephthalat-Nylon 6-Zweikomponentenfasern wurde mit Hilfe von DSC-Messungen untersucht. Es wurde eine Abnahme des Intervalls AT zwischen der Glasubergangstemperatur und der Temperatur der kalten Kristallisation gefunden. Es wurden auch hderungen der Temperatur der Schmelzkristallisation der beiden Komponenten beobachtet, die von den Mischungsanteilen abhtingen (z. B. Phasenmorphologie). Diese Effekte wurden mit einer physikalischen Grenzflachenwechselwirkung erklart, die den Ordnungsgrad der Molekiile innerhalb der Phase iindert. Eine Beziehung zwischen der Abnahme von AT der PETP Komponente und des Verstreckungsgradmaximums, Lm, von Zweikomponentenfasern wurde festgestellt. Es wird vermutet, da8 die Anderung von AT das Auftreten von lokalen Spannungen und den Beginn von Mikrorissen in der PETP-Phase verursacht, was zu einer Abnahme von A, , , , = fuhrt.

No abstract

No abstract

No abstract

No abstract