Due to its avascular nature, articular cartilage exhibits a very limited capacity to regenerate and to repair. Although much of the tissue-engineered cartilage in existence has been successful in mimicking the morphological and biochemical appearance of hyaline cartilage, it is generally mechanically inferior to the natural tissue. In this study, we tested the hypothesis that the application of dynamic deformational loading at physiological strain levels enhances chondrocyte matrix elaboration in cell-seeded agarose scaffolds to produce a more functional engineered tissue construct than in free swelling controls. A custom-designed bioreactor was used to load cell-seeded agarose disks dynamically in unconfined compression with a peak-to-peak compressive strain amplitude of 10 percent, at a frequency of 1 Hz, 3 x (1 hour on, 1 hour off)/day, 5 days/week for 4 weeks. Results demonstrated that dynamically loaded disks yielded a sixfold increase in the equilibrium aggregate modulus over free swelling controls after 28 days of loading (100 +/- 16 kPa versus 15 +/- 8 kPa, p < 0.0001). This represented a 21-fold increase over the equilibrium modulus of day 0 (4.8 +/- 2.3 kPa). Sulfated glycosaminoglycan content and hydroxyproline content was also found to be greater in dynamically loaded disks compared to free swelling controls at day 21 (p < 0.0001 and p = 0.002, respectively).

Deformational loading represents a primary component of the chondrocyte physical environment in vivo. This review summarizes our experience with physiologic deformational loading of chondrocyte-seeded agarose hydrogels to promote development of cartilage constructs having mechanical properties matching that of the parent calf tissue, which has a Young's modulus E(Y) = 277 kPa and unconfined dynamic modulus at 1 Hz G* = 7 MPa. Over an 8-week culture period, cartilage-like properties have been achieved for 60 x 10(6) cells/ml seeding density agarose constructs, with E(Y) = 186 kPa, G* = 1.64 MPa. For these constructs, the GAG content reached 1.74% ww and collagen content 2.64% ww compared to 2.4% ww and 21.5% ww for the parent tissue, respectively. Issues regarding the deformational loading protocol, cell-seeding density, nutrient supply, growth factor addition, and construct mechanical characterization are discussed. In anticipation of cartilage repair studies, we also describe early efforts to engineer cylindrical and anatomically shaped bilayered constructs of agarose hydrogel and bone (i.e., osteochondral constructs). The presence of a bony substrate may facilitate integration upon implantation. These efforts will provide an underlying framework from which a functional tissue-engineering approach, as described by Butler and coworkers (2000), may be applied to general cell-scaffold systems adopted for cartilage tissue engineering.

An automated approachfor measuring in situ two-dimensional strain fields was developed and validated for its application to cartilage mechanics. This approach combines video microscopy, optimized digital image correlation (DIC), thin-plate spline smoothing (TPSS) and generalized cross-validation (GCV) techniques to achieve the desired efficiency and accuracy. Results demonstrate that sub-pixel accuracies can be achieved for measuring tissue displacements with this methodology with a measurement uncertainty ranging from 0.25 to 0.30 pixels. The deformational gradients (from which the strains are determined) can be evaluated directly using the optimized DIC, with a measurement uncertainty of 0.017 to approximately 0.032. In actual measurements of strain in cartilage, TPSS and differentiation can be used to achieve a more accurate measurement of the gradients from the displacement data. Using this automated approach, the two-dimensional strain fields inside immature bovine carpometacarpal joint cartilage specimens under unconfined compression were characterized (n=21). The depth-dependent apparent elastic modulus and Poisson's ratio were also determined and found to be smallest at the articular surface and increasing with depth. The apparent Poisson's ratio is found to decrease with increasing compressive strain, with values as low as 0.01 observed near the articular surface at 25% compression. The variation of the apparent Poisson's ratio with depth is found to be consistent with a theoretical model of cartilage which accounts for the disparity in its tensile and compressive moduli.

No abstract

The precise nature of the material symmetry of articular cartilage in compression remains to be elucidated. The primary objective of this study was to determine the equilibrium compressive Young's moduli and Poisson's ratios of bovine cartilage along multiple directions (parallel and perpendicular to the split line direction, and normal to the articular surface) by loading small cubic specimens (0.9×0.9×0.8 mm, n=15) in unconfined compression, with the expectation that the material symmetry of cartilage could be determined more accurately with the help of a more complete set of material properties. The second objective was to investigate how the tension-compression nonlinearity of cartilage might alter the interpretation of material symmetry. Optimized digital image correlation was used to accurately determine the resultant strain fields within the specimens under loading. Experimental results demonstrated that neither the Young's moduli nor the Poisson's ratios exhibit the same values when measured along the three loading directions. The main findings of this study are that the framework of linear orthotropic elasticity (as well as higher symmetries of linear elasticity) is not suitable to describe the equilibrium response of articular cartilage nor characterize its material symmetry; a framework which accounts for the distinctly different responses of cartilage in tension and compression is more suitable for describing the equilibrium response of cartilage; within this framework, cartilage exhibits no lower than orthotropic symmetry.