With an increasing interest for molded pulp product (MPP) in the industry, it is important to fully understand how the manufacturing process is different from papermaking. One specific way to differentiate the processes is to compare their resulting products. As the paper industry uses several wood fibers with various pulping processes, it is interesting to compare some of these fibers, to further progress our understanding of the MPP process. In this study, six different wood fibers were used (as received) and analyzed to obtain the sample with the lowest moisture uptake and highest tensile properties. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and fiber analysis module (MorFi) observations were performed, as well as moisture uptake measurements after sorption and tensile tests. We observed significant differences between the fibers tested. Kraft fibers (bleached softwood kraft pulp (BSKP), bleached hardwood kraft pulp (BHKP), and unbleached softwood kraft pulp (USKP)) showed smoother surfaces and less non-cellulosic molecules, such as hemicellulose, lignin, and pectin, in the SEM images. Bleached chemi-thermomechanial pulp (BCTMP) and recycled pulps (R-NPM and R-CBB) both showed non-cellulosic molecules and rougher surfaces. These results were confirmed with the FTIR analysis. With kraft fibers, MPP mechanical properties were lower than non-kraft fibers. Resulting moisture uptake is in between the recycled fibers (lowest moisture uptake) and BCTMP (highest moisture uptake). The removal of non-cellulosic molecules reduces the mechanical properties of the resulting MPP. The incorporation of non-wood molecules, as found in recycled fibers, also reduces the mechanical properties, as well as moisture uptake, when compared with BCTMP.

This study was carried out using bleached softwood Chemi-Thermo-Mechanical Pulp to evaluate the influence of Molded Pulp Products’ manufacturing process parameters on the finished products’ mechanical and hygroscopic properties. A Taguchi table was done to make 8 tests with specific process parameters such as moulds temperature, pulping time, drying time, and pressing time. The results of these tests were used to obtain an optimized manufacturing process with improved mechanical properties and a lower water uptake after sorption analysis and water immersion. The optimized process parameters allowed us to improve the Young’ Modulus after 30h immersion of 58% and a water uptake reduction of 78% with the first 8 tests done.

This study was carried out using bleached softwood Chemi-Thermo-Mechanical Pulp to evaluate the influence of Molded Pulp Products’ manufacturing process parameters on the finished products’ mechanical and hygroscopic properties. A Taguchi table was done to make 8 tests with specific process parameters such as moulds temperature, pulping time, drying time and pressing time. The results of these tests were used to obtain an optimized manufacturing process with improved mechanical properties and a lower water uptake after sorption analysis and water immersion. The optimized process parameters allowed us to improve the Young’ Modulus after 1h immersion of 58% and a water uptake reduction of 78% with the first 8 tests done.