The aim of this work is to investigate the use of microtopographies in providing physical cues to modulate the cellular response of human mesenchymal stem cells on ceramics. Two microgrooved patterns (100 μm/50 μm, 10 μm/10 μm groove/pitch) were transcribed reversely onto alumina green ceramic tapes via an embossing technique followed by sintering. Characterization of the micropatterned alumina surfaces and their cellular response was carried out. Spread and polygonal cell morphologies were observed on the wider groove (50 μm/100 μm) surface. Cells seeded onto the narrow groove (10 μm/10 μm) surface aligned themselves alongside the grooves, resulting in more elongated cell morphology. More osteoid matrix nodules shown by osteopontin and osteocalcin biomarkers were detected on the larger grooved surfaces after cell culture of 21 days, indicating a greater level of osteogenicity. This study has shown that micropatterned wider groove (50 μm) topographies are more suitable surfaces for improving osseointegration of ceramic implants.

Surface topography is known to influence stem cells and has been widely used as physical stimuli to modulate cellular behaviour including adhesion, proliferation and differentiation on 2D surfaces. Integration of well-defined surface topography into three-dimensional (3D) scaffolds for tissue engineering would be useful to direct the cell fate for intended applications. Technical challenges are remaining as how to fabricate such 3D scaffolds with controlled surface topography from a range of biodegradable and biocompatible materials. In this paper, a novel fabrication process using computer numerically controlled machining and lamination is reported to make 3D calcium phosphate/gelatin composite scaffolds with integrated surface micropatterns that are introduced by embossing prior to machining. Geometric analysis shows that this method is versatile and can be used to make a wide range of lattices with porosities that meet the basic requirements for bone tissue engineering. Both in vitro and in vivo studies show that micropatterned composite scaffolds with surfaces comprising 40 μm pits and 50 μm grooves were optimal for improved osteogenesis. The results have demonstrated the potential of a novel fabrication process for producing cell-instructive scaffolds with designed surface topographies to induce specific tissue regeneration.

No abstract