Background Long-lasting insecticidal nets (LLINs) are expected to last for at least 3 years, but whilst this may be achieved from an insecticidal perspective, physical protection is frequently compromised much earlier because of the rapid accumulation of holes during use. To understand why LLINs are so susceptible to loss of physical integrity, thousands of hole damage sites in LLINs retrieved from the field in Africa and Asia were forensically studied to identify the persistent underlying causes. Methods A total of 525 LLINs consisting of six different brands from five different countries across Africa and Asia were collected from the field after 1 to 3 years in use. More than 42,000 individual sites of hole damage were analysed based on the morphology and size of each individual hole, aided by optical microscopy (OM) and scanning electron microscopy (SEM). The fracture morphology enabled positive identification of the underlying mechanisms of the damage. Results Across all LLINs and geographical settings, mechanical damage is the primary cause of holes and loss of physical integrity in LLINs (63.14% by frequency and 81.52% by area). Snagging is the single most frequent mechanical damage mechanism, whilst the largest sized holes in LLINs result from seam failure and tearing. Abrasion and hole enlargement are also responsible for a progressive loss in the physical integrity of nets. Collectively, these five modes of mechanical damage can be expected to result from normal use of LLINs by households. Evidence of deliberate cutting, burn holes and rodent damage was observed to a lesser degree, which LLINs are not designed to withstand. Conclusions Loss of physical integrity in LLINs is an inevitable consequence of using a vector control product that has an inherently low resistance to mechanical damage during normal use. To improve performance, new specifications based on laboratory textile testing is needed, to assess the resistance of LLIN products to the primary causes of mechanical damage when in use, which are snagging, tearing, abrasion and hole enlargement. Seam construction also needs to meet a revised minimum standard to reduce the risk of a rapid loss of physical integrity during use.

Background In common with the majority of personal protective equipment and healthcare products, the ability for long-lasting insecticidal nets (LLINs) to remain in good physical condition during use is a key factor governing fitness for purpose and serviceability. The inherent ability of a product to resist physical deterioration should be known in advance of it being used to ensure it has maximum value to both the end-user and procurer. The objective of this study was to develop a single performance metric of resistance to damage (RD) that can be applied to any LLIN product prior to distribution. Methods Algorithms to calculate RD values were developed based on consideration of both human factors and laboratory testing data. Quantitative reference forces applied to LLINs by users during normal use were determined so that aspirational performance levels could be established. The ability of LLINs to resist mechanical damage was assessed based on a new suite of textile tests, reflecting actual mechanisms of physical deterioration during normal household use. These tests quantified the snag strength, bursting strength, abrasion resistance and resistance to hole enlargement. Sixteen different unused LLINs were included in the analysis. The calculated RD values for all LLINs and the corresponding physical integrity data for the same nets retrieved from the field (up to 3 years of use) were then compared. Results On a RD scale of 0 (lowest resistance) – 100 (highest resistance), only six of the sixteen LLINs achieved an RD value above 50. No current LLIN achieved the aspirational level of resistance to damage (RD = 100), suggesting that product innovation is urgently required to increase the RD of LLINs. LLINs with higher RD values were associated with lower hole damage (PHI) in the field when adjusted for normal use conditions. Conclusions The RD value of any LLIN product can be determined prior to distribution based on the developed algorithms and laboratory textile testing data. Generally, LLINs need to achieve higher RD values to improve their ability to resist hole formation during normal use. Innovation in LLIN product design focused on the textile material should be actively encouraged and is urgently needed to close the performance gap.

Plant breeding is achieved through the controlled self- or cross-pollination of individuals and typically involves isolation of floral parts from selected parental plants. Paper, cellulose or synthetic materials are used to avoid self pollination or cross contamination. Low seed set limits the rate of breeding progress and increases costs. We hypothesized that a novel ‘non-woven’ fabric optimal for both pollination and seed set in multiple plant species could be developed. After determining the baseline pollen characteristics and usage requirements we established iterative three phase development and biological testing. This determined (1) that white fabric gave superior seed return and informed the (2) development of three non-woven materials using different fibre and layering techniques. We tested their performance in selfing and hybridisation experiments recording differences in performance by material type within species. Finally we (3) developed further advanced fabrics with increased air permeability and tested biological performance. An interaction between material type and species was observed and environmental decoupling investigated, showing that the non-woven fabrics had superior water vapour transmission and temperature regulation compared to controls. Overall, non-woven fabrics outperformed existing materials for both pollination and seed set and we found that different materials can optimize species-specific, rather than species-generic performance.

Background LLINs are susceptible to forming holes within a short time in use, compromising their ability to provide long-term physical protection against insect-borne vectors of disease. Mechanical damage is known to be responsible for the majority of holes, with most being the result of snagging, tearing, hole enlargement, abrasion and seam failure, which can readily occur during normal household use. To enable an assessment of the ability of LLINs to resist such damage prior to distribution, a new suite of testing methods was developed to reflect the main damage mechanisms encountered during normal use of LLINs. Methods Four existing BS EN and ISO standards used by the textile industry were adapted to determine the ability of LLINs to resist the most common mechanisms of real-world damage experienced in the field. The new suite comprised tests for snag strength (BS 15,598:2008), bursting strength (ISO 13938-2:1999), hole enlargement resistance (BS 3423–38:1998), abrasion resistance (ISO 12947-1:1998) and new guidance around the seam construction of LLINs. Fourteen different LLINs were tested using the new suite of tests to evaluate their resistance to damage. Results The resistance to mechanical damage of LLINs is not the same, even when the bursting strength values are comparable. Differences in performance between LLINs are directly related to the fabric design specifications, including the knitted structure and constituent yarns. The differences in performance do not primarily relate to what polymer type the LLIN is made from. LLINs made with a Marquisette knitted structure produced the highest snag strength and lowest hole enlargement values. By contrast, LLINs made with a traverse knitted structure exhibited low snag strength values when compared at the same mesh count. Conclusions Prequalification of LLINs should consider not only insecticidal performance, but also inherent resistance to mechanical damage. This is critical to ensuring LLINs are fit for purpose prior to distribution, and are capable of remaining in good physical condition for longer. The new suite of test methods enables the performance of LLINs to be assessed and specified in advance of distribution and can be used to establish minimum performance standards. Implementation of these testing methods is therefore recommended.

Background Attempts have been made to link procurement of long-lasting insecticidal nets (LLIN) not only to the price but also the expected performance of the product. However, to date it has not been possible to identify a specific textile characteristic that predicts physical durability in the field. The recently developed resistance to damage (RD) score could provide such a metric. This study uses pooled data from durability monitoring to explore the usefulness of the RD methodology. Methods Data from standardized, 3-year, prospective LLIN durability monitoring for six LLIN brands in 10 locations and four countries involving 4672 campaign LLIN were linked to the RD scores of the respective LLIN brands. The RD score is a single quantitative metric based on a suite of standardized textile tests which in turn build on the mechanisms of damage to a mosquito net. Potential RD values range from 0 to 100 where 100 represents optimal resistance to expected day-to-day stress during reasonable net use. Survival analysis was set so that risk of failure only started when nets were first hung. Cox regression was applied to explore RD effects on physical survival adjusting for known net use environment variables. Results In a bivariate analysis RD scores showed a linear relationship with physical integrity suggesting that the proportion of LLIN with moderate damage decreased by 3%-points for each 10-point increase of the RD score (p = 0.02, R2 = 0.65). Full adjustment for net care and handling behaviours as well as other relevant determinants and the country of study showed that increasing RD score by 10 points resulted in a 36% reduction of risk of failure to survive in serviceable condition (p < 0.0001). LLINs with RD scores above 50 had an additional useful life of 7 months. Conclusions This study provides proof of principle that the RD metric can predict physical durability of LLIN products in the field and could be used to assess new products and guide manufacturers in creating improved products. However, additional validation from other field data, particularly for next generation LLIN, will be required before the RD score can be included in procurement decisions for LLINs.